The glucopyranose forms of glucose predominate in solution, and are the only forms observed in the solid state.
葡萄糖的吡喃糖形式在溶液中占优势，并且是在固态中观察到的唯一形式。
The results show that Cu solubilizes in W and the substitutional solid solution is formed.
结果发现，铜固溶在钨中，并形成了置换固溶体。
Problems in the negotiations, both sides should have a sense of urgency, step by step, a solid solution.
对谈判中存在的问题，双方应有紧迫感，一步一步扎实加以解决。
A solid solution of ferric carbide or carbon in iron; cools to form pearlite or marten site.
含铁碳化物或含碳铁的固体溶体，冷却可形成珠光体或马氏体。
The iron wants to change from the FCC austenite structure to the BCC ferrite structure, but the ferrite can only contain 0.02% carbon in solid solution.
铁需要从面心立方体奥氏体结构转变为体心立方体铁素体结构，但是铁素体只能容纳固溶体状态的0.02%的碳。
However, further increase of the concentration results primarily in solid solution precipitation.
平衡浓度进一步增大，以固体溶液沉积为主。
At the upper temperatures, only austenite is present, the 0.77% carbon being dissolved in solid solution with the iron.
在较高温度时，只存在奥氏体，0.77%的碳溶解在铁里形成固溶体。
Alloy: Metallic substance composed of two or more elements, as either a mixture, compound, or solid solution.
合金：由两种或多种元素组成的金属材料，以化合物或固溶体形式存在。
It was shown by the measured activities and calculating models that there isn t any effect of common ions in molten salts involving solid solution, compound as well as peritectic.
从实测活度和计算模型证明含固熔体、含化合物和含包晶体的熔盐中没有共同离子的任何作用。
A entirely set of method to separate and determine solid solution boron, carbon boride, alloy elements boride, boron oxide and boron nitride in low boron steel is established.
通过实验，建立了一整套低硼钢中固溶硼、碳硼化物、合金元素硼化物、氧化硼和氮化硼的分离、测定方法。
World leaders are running out of time to come up with a solid solution before that meeting.
要在哥本哈根气候大会之前达成一个切实可行的解决方案，世界上各国领导人的时间已经所剩无几。
In addition, the metal body within welding heat effect zone will produce a lot of micro-cracks because of infiltration of solid solution nitrogen in course of porcelain spraying.
此外，喷瓷管道焊接热影响区的金属基体将由于喷瓷过程中渗入的固溶氮而产生大量微裂纹。
Thus in the depth of the valence electron theory of solid solution the mechanical behavior of the alloy elements in martensite was shown.
从而在固溶态价电子理论的深度揭示了合金元素在马氏体中的力学行为。
Morphology transformation of eutectic silicon in Al-Si alloy during solid solution was observed by OM and SEM.
通过金相和扫描电镜观察研究了铸造铝硅合金中的共晶硅在固溶热处理过程中的形态变化。
Uniform corrosion happened on homogeneous H13. Corrosion resistance of compound phase is better than solid solution phase, whether in Fe-based superalloy or Co-based superalloy.
H 13材料的显微组织均一，发生均匀腐蚀，多相的铁基超合金和钴基超合金显微组织中化合物相比固溶体相耐锌腐蚀性能好。
The influence of different ratio of raw materials on crystalline phases and unit cell parameters were studied and the formation mechanism of mullite solid solution was discussed.
探讨不同配方合成的莫来石的晶相组成、晶胞参数及带有结构缺陷的莫来石固溶体的形成机理。
The influence of different solid solution treatment on the structure and corrosion resistant property of cast duplex stainless steel was investigated.
研究了不同固溶处理对双相铸造不锈钢的组织及其耐蚀性能的影响。
The main strengthening mechanisms of (Ti, Cr)N films were grain fining, solid solution strengthening and multi elements strengthening.
多元膜层强化机理主要是：晶粒细化、固溶强化、多元素优化。
It has low melting point and good wettability to the base-metal, and contains a high-strength and high-hardness solid solution structure, with a high strength of soldering joint.
该钎料具有熔点低，对母材的润湿性好，钎焊接头组织中含有强度、硬度较高的呈弥散分布的固溶体，以及接头强度较高等特点。
Vanadium nitride and carbide, as a solid solution, is an important additive to steel.
碳氮化钒是氮化钒和碳化钒的固溶体，是重要的钢中添加剂。
It is shown that the mechanical properties of annealed sample of 2224 aluminum alloy are improved by the combination of solid solution and aging treatment after ECAP, the size of grain is refined.
结果表明，退火态2224铝合金经e CAP挤压后，进行固溶和时效处理，明显提高了合金的力学性能，细化了合金的晶粒。
Solid solution strengthening is summarized and compared to the new concept for this lecture: precipitation strengthening.
将摘要固溶强化并与本堂课的新观念-析出强化进行比较。
Vanadium base solid solution hydrogen alloy is a kind of the high performance materials developed in recent years.
钒基固溶体贮氢合金是近年来开发的一种新型高性能贮氢材料。
The increasing of conductivity is the decomposition of the supersaturate solid solution contain Sc and Zr forming dispersion complex phase.
电导率的增加是含钪锆过饱和固溶体的分解形成弥散型的复相结构。
The effect of solid solution temperature on the structure properties of LY11 aluminium alloy is studied.
本文研究了固溶温度对硬铝LY11组织与性能的影响。
Up to now, the technology has been used to prepare supersaturated solid solution, amorphous alloys, intermetallic compound, nanocrystalline, magnetism materials, superconductor materials, and etc.
现在，运用这一技术已成功制备出过饱和固溶体、非晶、金属间化合物、纳米晶材料和超导材料、磁性材料等。
Compared with NM2, NM1 had higher specific surface area and smaller crystallites size of nickel-magnesian solid solution, and after reduction NM1 also had smaller size of nickel crystallites.
与NM2相比，NM1具有较大的比表面和较小的镍镁固溶体晶粒度，还原后的NM1催化剂中镍晶粒也相对较小。
Hard anodizing film could be obtained on Al-Cu alloy surface which had been treated with solid solution treatment and natural aging.
经固溶处理和自然时效的铝铜合金可以进行硬质阳极氧化。
The microstructure and properties of chromium bronze after homogenizing treatment, solid solution and aging treatment, cool deformation and aging was studied.
研究了均匀化处理、固溶时效、冷变形时效等对铬青铜显微组织和性能的影响。
The microstructure and properties of chromium bronze after homogenizing treatment, solid solution and aging treatment, cool deformation and aging was studied.
研究了均匀化处理、固溶时效、冷变形时效等对铬青铜显微组织和性能的影响。