An improved TMS method is used to study zeolite Ld-steel slag cement.
本文利用改进了的三甲基硅烷化方法研究低熟料沸石钢渣水泥。
Usually steel slag is used as metallurgical materials, cement, roadbed materials, construction materials and phosphate fertilizer.
普通钢渣经处理可作冶金原料、水泥、路基材料等建筑用料和磷肥。
Steel slag is not better to produce cement or mineral admixture of concrete because of poor grindability, larger fluctuation of chemical and mineral components, poor stability and so on.
由于钢渣成份波动大、易磨性差以及稳定性不好，钢渣用作水泥混合材或混凝土掺合料均难以达到高效、高值化利用的目的。
By test analysis compared with strength degree 32.5 of cement, strength of steel slag concrete is slightly decreased, but its fluidity is improved.
实验对比表明：与强度等级为32 . 5的纯水泥钢渣混凝土对比，掺入钢渣粉的砼强度略有降低，但能改善混凝土的和易性。
Theoretical studies are carried out on the slag of tilting converters in Baoshan Steel Works as an cement addition and the possibilities to make blended cement with other additions.
本文针对转炉钢渣能否作为混合材的课题对宝钢转炉钢渣进行了一些理化研究，并且探讨与其它混合材一起掺入水泥中生产混合水泥的可能性。
Small amount of steel slag was used as low quality clinker in high addition of slag cement to compensate the lack of alkalinity caused by low clinker addition.
在高掺量矿渣水泥中掺少量可看作低质熟料的钢渣，弥补由于熟料掺量少造成的碱性不足。
The paper deals with production of cement from blast-furnace slag and steel-smelting furnace slag, especially with manufacture process and use of the cement.
本文介绍利用工业废渣—钢渣生产钢渣矿渣水泥，着重介绍钢渣矿渣水泥的生产工艺和应用。
By dosing external additive during the steel smelting in the revolving furnace, the chemical content of the slag can be made similar to that of silicate cement.
在转炉炼钢的过程中添加少量外加剂，调整冶炼渣的化学成分，使其接近普通硅酸盐水泥熟料的化学成分。
This series of products can be used for limestone, cement guessed, mixed materials, gypsum, coal gangue, porcelain, glass, slag, steel ore, iron ore and other materials, the final Fenmo.
本系列产品可用于石灰石、水泥孰料、混合料、石膏、煤矸石、陶瓷、玻璃、矿渣、钢矿石、铁矿石等各种物料的终粉墨。
This series of products can be used for the final crushing of limestone, cement guessed, mixed materials, gypsum, coal gangue, porcelain, glass, slag, steel ore, iron ore and other materials.
本系列产品可用于石灰石、水泥孰料、混合料、石膏、煤矸石、陶瓷、玻璃、矿渣、钢矿石、铁矿石等各种物料的终粉墨。
Combined with the applying practice in Kunming Iron-steel Jiahua cement co. Ltd., the paper analyzes the application property of slag powder mixed in cement and concrete.
结合昆钢嘉华公司矿渣微粉的应用实际，对矿渣微粉在水泥和混凝土中的应用性能进行了分析。
The effects of matrix structure and interface situation on properties of plant fiber cement-based composite materials with steel slag were studied.
针对含有钢渣的植物纤维增强水泥基复合材料，研究了其基体结构和界面状况对材料性能的影响。
In the paper, 10%-20% clinker and lots of waste slag, such as slag, steel slag, were used to prepared green cementing materials with the grade of cement 325 or 425.
本文试验用10% - 20%的水泥熟料及大量的以矿渣和钢渣为主的工业废渣，配置出325、425号绿色复合水泥。
Chemical and physical properties and expansive property have been studied for steel slag expansive cement.
研究了硅酸盐水泥添加钢渣膨胀剂后的物理化学性能和膨胀性能。
By orthogonal test, the research on preparing a composite Portland cement using steel slag was processed in this study.
通过正交试验进行了利用钢渣配制复合硅酸盐水泥的初步研究。
The effect of water binder ratio (W/C), slag binder ratio (S/C) as well as the adding quantity of steel fiber on cement based composite was studied;
研究了水灰比（W/C）、砂灰比（S/ C）、钢纤维掺量对水泥基复合材料性能的影响；
The paper introduces the quality control methods and results achieved in construction of cement-stabilized steel slag pavement base.
介绍了水泥稳定钢渣路面基层施工过程中的质量控制方法及达到的效果。
525and 425 ordinary Portland cement, 525 composite Portland cement, 425 steel slag Portland cement can be produced with the addition of pulverized steel slag with enough fineness.
用足够细的磨细钢渣粉可以制成525普通硅酸盐水泥、525复合硅酸盐水泥、425复合硅酸盐水泥和钢渣矿渣水泥。
The workability, strength, setting time and shrinkage of cement mortars with Bao Steel rotating furnace slag (BSRS) or electric furnace slag (EFS) as substitute for sand were studied.
研究了宝钢转炉滚筒渣、电炉渣代砂建筑砂浆的和易性、强度、凝结时间和收缩等性能。
The effect of mineral blenders includes ground steel slag and fly ash on the electrical conductivity of cement mortar was studied.
试验研究了掺加磨细钢渣、粉煤灰等掺合料后水泥浆体导电性能的变化。
But the factor of the steel slag fine and aging times have relatively more and more significant influence on the later compressive strength and the cement content is still the most influential factor.
对于后期强度，水泥含量虽影响最大，但钢渣细度和陈化龄期的影响明显增强。
The research indicated that, the Portland cement had a best effect to enhance the activity of steel slag when the admixture amount of steel slag was less than 30%.
研究表明，钢渣掺入量<30%时，硅酸盐水泥对钢渣的活性激发效果最好；
The Portland cement was used as an activator to improve the hydration activity of steel slag.
试验研究了在硅酸盐水泥体系中通过碱性激发提高钢渣水化活性的方法。
The strength synergistic effect of each component on composite Portland cement with fly ash, slag, steel slag and a certain amount of clinker and its influence factors are studied.
研究了由粉煤灰、矿渣、钢渣与一定量熟料组成的粉煤灰矿渣复合水泥中各组分对水泥的强度协同效应以及影响协同效应的主要因素。
Rusults show that mobility of cement paste can be improved when steel slag is added to cement.
结果表明，钢渣掺入水泥中可以改善水泥浆体的流动性。
Steel slag and mixing with blast furnance slag influent on performances of cement paste was discussed.
主要研究单掺钢渣以及钢渣与矿渣复合后对水泥浆体各项物理力学性能的影响。
A good linear relationship meet between fractal dimension and specific surface area of slag powder, and positive correlation with the cementitious properties of steel slag-based cement material.
分形维数与钢渣微粉的比表面积间满足良好的线性关系，并与钢渣基水泥材料的胶凝性能良性相关。
The phenomenon can see from the SEM that, after the exciting of acid, steel slag process to secondary hydration together with cement clinker, combining to a great deal of meshy gelatin.
从SEM照片看出，钢渣在酸性激发剂作用下，与熟料水化产物发生二次水化，相互联结在一起，形成大量的网状结构的絮状凝胶。
The phenomenon can see from the SEM that, after the exciting of acid, steel slag process to secondary hydration together with cement clinker, combining to a great deal of meshy gelatin.
从SEM照片看出，钢渣在酸性激发剂作用下，与熟料水化产物发生二次水化，相互联结在一起，形成大量的网状结构的絮状凝胶。