Fatigue specimens cracked at two-sided through-thickness sheet, fatigue crack appeared initially in HAZ of inner surface of lap plates, along the thickness direction extended to outer surface;
试件的疲劳断裂模式全部为双面穿板断裂，疲劳裂纹起始于点焊热影响区搭接板内表面，沿板厚方向向外表面扩展；
Fatigue specimens cracked at two-sided through-thickness sheet, fatigue crack appeared initially in HAZ of inner surface of lap plates, along the thickness direction extended to outer surface;
试件的疲劳断裂模式全部为双面穿板断裂，疲劳裂纹起始于点焊热影响区搭接板内表面，沿板厚方向向外表面扩展；