The formulae for calculating SIF and fatigue life of surface crack at weld toe of the high-strength steel under the combination stresses were given out.
给出了高强钢焊趾表面裂纹在压弯组合应力下应力强度因子及其疲劳寿命计算式。
The formulae for calculating SIF and fatigue life of surface crack at weld toe of the high-strength steel under the combination stresses have been presented.
给出高强钢焊趾表面裂纹在压弯组合应力下应力强度因子及其疲劳寿命计算式。
The fatigue crack propagation rate of the fusion line and weld toe are greater than that of the others.
熔合线和焊趾处疲劳裂纹扩展速率较其他部位大。
The second crack is a crack originating at the groove weld toe of the column flange-girder flange connection.
第二种是产生于立柱翼缘与主梁翼缘连接处的坡口焊缝焊趾处的裂纹。
The second crack is a crack originating at the groove weld toe of the column flange-girder flange connection.
第二种是产生于立柱翼缘与主梁翼缘连接处的坡口焊缝焊趾处的裂纹。