对不同变形量的合金丝进行了再结晶退火试验。
The recrystallization behaviours of Ta-Ti alloy wires with various deformation degrees were studied.
本论文选用工业纯铜板材作为研究对象，对其进行了不同道次的异步叠轧和再结晶退火实验。
In this paper, the copper sheets were subject to asymmetrical accumulative rolling-bonding (AARB) by different passes and recrystallization annealing.
研究结果表明，双金属材料确定后，热处理芯轴尺寸和再结晶退火温度决定双金属环的最终尺寸。
The research result indicates that, when bimetal material is certain, the size of heat treatment mandrill and the temperature of re-crystallized anneal would decide the end size of bimetals wreaths.
对形变后的试样进行再结晶退火后发现，再结晶形核机制为晶界弓出形核，晶界弓出方向为储存能较高的晶粒。
Upon annealing of the deformed samples, nucleation takes place at the original grain boundaries a nd the nuclei grow into the local region with the highest stored energy.
研究了工业纯铜T2在77K温度下快速压缩变形的组织变化和再结晶退火温度、时间对其组织、性能的影响。
The microstructure and hardness of T2 copper subjected to stamping deformation at 77 K and subsequently recrystallization annealing were studied.
退火后，孪晶逐渐消失，形成等轴的再结晶晶粒。
The twins disappeared gradually and recrystallized grains formed after annealing.
退火后，孪晶逐渐消失，形成等轴的再结晶晶粒。
The twinning disappeared gradually and recrystallized grains formed after annealing.
应用取向分布函数(odf)研究和分析了3104铝合金经不同工艺退火后的再结晶织构。
The recrystallization textures after different annealing processes of 3104 aluminium alloy had been investigated by means of orientation distribution functions (ODFs).
实验表明：在退火条件下，再结晶织构对腐蚀铝箔的电容量有重要影响。
The experimental results showed that in the annealing condition the recrystallization texture has an important influence on the capacitance of etched al foil.
退火过程中析出的二次碳化物阻碍再结晶晶界的迁移，从而影响再结晶层的界面推移速率。
The secondary carbides have a strong influence on recrystallization rate by retarding the migration of recrystallization grain boundaries.
不锈钢经过热轧后，需经罩式炉退火工艺使材料充分再结晶后才能投入使用。
After hot rolling, only through full recrystallizing by annealing process in the batch, can the stainless steel be put into use.
采用晶体取向分布函数（ODF）、TEM研究了铁含量及退火对高纯铝箔再结晶织构的影响。
The influence of trace Fe and annealing on recrystallization texture of high purity aluminum foils was investigated by means of orientation distribution functions(ODFs)and TEM.
分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。
The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.
结果表明，该模型能很好地描述无间隙原子钢等温退火再结晶过程。
The result shows that the model can be used to describe the recrystallization process of the interstitial free steel quite well.
结果表明，该模型能很好地描述无间隙原子钢等温退火再结晶过程。
The result shows that the model can be used to describe the recrystallization process of the interstitial free steel quite well.