研制出了抗冲击韧性水泥外加剂。
We research and manufacture impact toughness cement additive.
钢中夹杂物对冲击韧性不利。
研究了微量钛对低碳硼钢冲击韧性的影响。
The effect of tiny amount of Titamium on the notch toughness of low carbon boron steel was investigated.
研究了热变形量对钒白口铸铁冲击韧性的影响。
The effect of hot deformation amount on impact toughness for Vanadium white cast iron was studied.
CTOD性能可作为修订常规冲击韧性标准的依据。
The CTOD toughness can be used as the basis to amend the conventional impact toughness criterion.
结果表明，随着时效温度的升高，冲击韧性呈下降趋势。
The results indicate that impact toughness of alloy will descend with ageing Treatment temperature increasing.
研究了具有不同微观组织类型的高强度管线钢的夏比冲击韧性。
The Charpy impact properties of high strength pipeline steel with different microstructure were investigated.
退火以后，发现材料的晶粒长大，材料的冲击韧性与延性提高。
After annealing coarse grain structure was observed and the impact ductility and the elongation of materials increased.
认为磷共晶加剧了碳化物的网状分布，降低了冲击韧性及耐磨性。
Eutectic phases of phosphorus aggravate the netting of carbides and result in the decreases to compact toughness and wear resistance.
高温制取的wc粉所配制的合金具有高的冲击韧性和良好的使用性能。
Alloys prepared by using WC powders with higher preparation temperatures are proven to have high impact toughness and good utility properties.
切削刀具最重要的性能是在高温下能保持的硬度、耐磨损和冲击韧性。
The most important properties of cutting tools are hardness at high temperature, wear resistance, and impact strength.
常用的做法是根据管材的冲击韧性与断裂韧性之间的关系式进行估算。
According to empirical equation between the Charpy impact energy and fracture toughness to estimate is common method.
对刮痕强度试验机进行适当的改进，就可测量芯砂的冲击韧性，并使一机两用。
The scratch strength tester has been improved in the paper, which can measure the impact toughness and has two uses.
在性能方面，强度被显著地提高，机械疲劳性能变化不明显，冲击韧性和塑性降低。
On mechanical properties, the strength was raised obviously, fatigue property was unchanged, impact toughness and ductility were reduced.
通过净化合金液，细化基体晶粒，细化碳化物可使铬合金白口铸铁的冲击韧性提高。
By purifying the alloy melt, refining matrix grain and carbide, it is possible to increase the impact toughness of the Cr-alloyed white cast iron.
黄麻纤维掺入聚丙烯导致黄麻纤维增强聚丙烯试样的冲击韧性摘要与断裂韧性下降。
The impact toughness and fracture toughness of the composite samples decrease after adding jute fibers when compared to pure polypropylene.
MIM制造是理想，要求接近全密度、高冲击韧性、高断裂韧性、耐疲劳和耐腐蚀性。
MIM fabrication is ideal where near-full density, high impact toughness, fracture toughness, and fatigue and corrosion resistance are required.
利用锻造方法并结合锻后适当的热处理工艺可大幅度提高铬合金白口铸铁的冲击韧性。
Adopting forging method and proper heat treatment after forging can improve significantly the impact toughness of chromium alloy white cast iron.
经含钡合金处理的钢材力学性能，如疲劳、横向冲击韧性和各向异性可得到显著改善。
The mechanical properties such as fatigue, transverse impact toughness and anisotropic properties of steels treated with Ba-containing alloys are remarkably improved.
在大量生产实践的基础上分析了影响ERW直缝电阻焊钢管焊缝冲击韧性的各种因素。
The article analyzes that all factors effect impacting toughness of welded seam of ERW pipe on the basis of mass produce and practice.
采用LD钢制造大型滚子冷镦模具的模芯，具有较理想的硬度、强度、耐磨性和冲击韧性。
Core of large roller cold upsetting die made of ld steel has more ideal hardness, strength, anti wear capacity and impact toughness.
研究了正火处理对FAS390Q桥壳钢显微组织、强度、冲击韧性和韧脆转变温度的影响。
The effect of normalizing on microstructure, strength, impact toughness and ductile-brittle transition temperature of FAS390Q axle housing steel was studied.
其中针状铁素体之间细小的马氏体的存在与数量对钢的抗拉强度和低温冲击韧性起关键作用。
The existence and amount of small isolated martensite between the acicular ferrite play an important role in determining the tensile strength and low temperature impact toughness of the steels.
通过对冲击韧性的测试结果与微观组织的分析，确定出使焊缝冲击韧性最佳的焊接工艺参数。
Meanwhile the optimal welding parameter which was suitable for welding line impact toughness was gained by analysis on the test result of impact toughness and microstructure.
因此在通常材料中所存在的各向异性完全消失，特别是缺口冲击韧性横向性能值提高了2～3倍。
The anisotropic characteristic which usually exists in materials disappeared completely especially the notch - impact toughness at the transverse direction was increased by 2-3 times.
试验表明，在T（10）钢中添加稀土元素对硬度没有明显的影响，但能显著改善该钢的冲击韧性。
The results show that RE additive may improve considerably the impact toughness and has little effect on hardness of steel T10.
采用上述工艺参数对浆料进行半固态挤压成形，并对挤压件进行冲击韧性、硬度和冲击磨料磨损测试。
Use these technical parameters, carry the semisolid extrusion shaping to the slurry, then test the impact ductility, rigidity and impacting grinding abrasion.
焊后试件的性能测试结果表明，焊接接头的拉伸强度、断面收缩率、延伸率及冲击韧性均已超过母材。
The results of performance measurement test show that tensile-strength, contraction of cross sectional area, elongation percentage, dynamic ductility of the weld all exceed their base metal.
结果表明，本钢X70管线钢具有高强度、高抗动态撕裂能力、高低温冲击韧性以及低韧脆转变温度。
The results indicate that the X70 pipeline steel with acicular ferrite microstructure has high strength, high toughness, low transition temperature and high dynamic tear-resistance.
结果表明，本钢X70管线钢具有高强度、高抗动态撕裂能力、高低温冲击韧性以及低韧脆转变温度。
The results indicate that the X70 pipeline steel with acicular ferrite microstructure has high strength, high toughness, low transition temperature and high dynamic tear-resistance.