本文首先是合成耐高温有机硅树脂。
采用红外光谱表征了端乙烯基超支化有机硅树脂的结构。
The structure of vinyl-ended hyperbranched organosilicon resin is characterized by FT-IR.
是由玻璃纤维纱编织成管后经高温处理，涂以有机硅树脂而成。
By the glass fiber yarn woven into a tube at high temperature treatment, silicone resin coating to form.
综述了近年来国内外有机硅树脂在粉末涂料中的应用研究进展。
The recent research progress in the silicone modified powder coatings is reviewed.
研究了含有有机硅树脂为囊心的液体微胶囊复合镀铜层的性能。
Properties of the composite copper coating with liquid microcapsule were studied.
有机硅树脂涂料是一类被广泛应用的重要材料，具有多种优良性能。
Organosilicon coatings is a kind of important materials applied widely with many excellent properties.
通过比较不同种类的有机硅树脂的耐热性能，筛选出合适的有机硅树脂。
The proper resin is figured out by comparing the heat resistance of different organosilane resins.
电阻器是用一种耐高温的有机硅树脂和硅粉作基本材料封装的功率型绕线电阻。
This resistor is power wire wound resistor which is made by a kind of organic silicon rosin and silicon powder as basic material encapsulation.
叙述了氟化改性有机硅树脂涂料的含义和特点，对其性能和在涂料中应用作了介绍。
This article presents the meaning and the characteristic of fluorinated organosilicon coatings and introduces their performances and the use in coatings.
我们用热重、差热和红外光谱法研究了GS-401烧蚀有机硅树脂的热降解反应。
The thermodegradation of GS-401 ablative silicone resin was studied with TG, DTA and IR.
重点介绍了酚醛树脂、有机硅树脂、磷酸盐等系列耐烧蚀复合材料的研究进展及应用。
This paper focuses on the development and application of the composites based on phenolic resin , silicone resin and phosphate.
介绍了有机硅树脂的品种及产品形态，以及甲基硅树脂和甲基苯基硅树脂的合成及应用。
The varieties and morphologies of silicone resin products, as well as the synthesis and application of methyl silicone resin and methyl phenyl silicone resins are described in this paper.
以环氧改性有机硅树脂为基体，氮化硅、氧化铝混合填料为导热粒子制备了导热绝缘涂料。
The thermal conductive coating was obtained with the epoxy modified silicone resin as matrix, and the mixture of silicone nitride and alumina as the heat conductive fillers.
结果表明：热处理温度对有机硅树脂结合不烧铝碳滑板的性能、物相变化和显微结构影响显著。
Results showed that heat treatment temperatures affected the properties, phase evolution and microstructure of the specimens remarkably.
采用傅里叶变换红外光谱表征了聚甲基丙烯酸丁酯（PBMA）共混改性有机硅树脂前后的结构特征；
The molecular structure of the silicone resin pre-and post-blending modification by poly (butyl methacrylate)(PBMA) was characterized by Fourier transform infra-red spectrometry.
以甲基和苯基氯硅烷为单体，采用水解缩聚的方法合成有机硅树脂，并对影响有机硅树脂合成的有关因素进行了研究。
The silicone resin is synthesized using hydrolysis-polycondensation method from phenyl and methyl chlorosilane, and the factors influencing this synthesis are investigated.
通过配方设计，确定以环氧改性有机硅树脂为基体，以硼酸盐等为体质填料，按一定配比配制一种新型气动热防护涂料。
Based on analysis and test, the silicone matrix resins modified by epoxy and borate etc was selected, which were confected an aero-dynamic heat-resist coating.
将玻璃填料、有机硅树脂、溶剂等其它助剂按一定比例配制成高温涂料，进行耐高温性、柔韧性、干燥时间、附着力等性能的测试。
The effect of sintering process and glass content on the coating properties was researched. A heat-resistant silicone resin is selected as a good coating of organic material by TGA and IR test.
目的：测定涂布超硬石膏表面硬化剂有机硅树脂前后石膏模型的表面硬度和抗磨损性能，为该石膏表面硬化剂的临床应用提供依据。
The superficial hardening of non-quenched steels had been carried out on a surface grinder, the influences of grinding mode and cooling conditions on the surface hardened layer were studied.
用环氧和有机硅树脂涂料对由聚乙烯／炭黑（PE／CB）制备的正温度系数（PTC）电路保护元件的表面处理及其工艺进行了研究。
The packaging materials and processes of positive temperature coefficient (PTC) devices made up of the composite of polyethylene and carbon black(PE/CB) for over current protection were studied.
采用有机硅树脂对精纺纯毛织物进行防毡缩整理，整理后的织物面积毡缩率、经向和纬向收缩率都达到“机可洗”标准，其他各项性能指标都较好。
After finished with silicone resin, the anti felt shrinkage and warp and wept shrinkage of 100% wool worsted fabric could be kept in "machine washable" standards with other feature index excellent.
采用有机硅树脂对精纺纯毛织物进行防毡缩整理，整理后的织物面积毡缩率、经向和纬向收缩率都达到“机可洗”标准，其他各项性能指标都较好。
After finished with silicone resin, the anti felt shrinkage and warp and wept shrinkage of 100% wool worsted fabric could be kept in "machine washable" standards with other feature index excellent.
应用推荐