以聚氧化丙烯二醇和甲苯二异氰酸酯、一缩二乙二醇等为主要基体材原料，以联二脲（LDA）、聚磷酸铵（APP）作为阻燃剂，制作了聚醚聚氨酯弹性体。
Polyether polyurethane elastomer material was prepared based on polypropylene oxide glycol, toluene diisocyanate (TDI) and DEG as main base meterial, LDA and APP as flame retardants.
采用三官能度的聚氧化丙烯醚醇、聚乙二醇，合成了吸水膨胀率在0～200%的聚氨酯弹性体。
Using tri-functionality polyoxytrimethylene alcohol ether and polyethylene glycol, synthetize polyurethane elastomer with water absorption expansion rate of0~200%.
采用三官能度的聚氧化丙烯醚醇、聚乙二醇，合成了吸水膨胀率在0～200%的聚氨酯弹性体。
Using tri-functionality polyoxytrimethylene alcohol ether and polyethylene glycol, synthetize polyurethane elastomer with water absorption expansion rate of0~200%.