再结晶织构的强度趋于一致。
实验表明：在退火条件下，再结晶织构对腐蚀铝箔的电容量有重要影响。
The experimental results showed that in the annealing condition the recrystallization texture has an important influence on the capacitance of etched al foil.
这些再结晶织构与冷轧织构之间存在与某些重合点阵关系相近的位向关系。
Orientation relationships between the annealing textures and the rolling textures were found to be close to some coincidence lattice relationships.
应用取向分布函数(odf)研究和分析了3104铝合金经不同工艺退火后的再结晶织构。
The recrystallization textures after different annealing processes of 3104 aluminium alloy had been investigated by means of orientation distribution functions (ODFs).
采用晶体取向分布函数（ODF）、TEM研究了铁含量及退火对高纯铝箔再结晶织构的影响。
The influence of trace Fe and annealing on recrystallization texture of high purity aluminum foils was investigated by means of orientation distribution functions(ODFs)and TEM.
结果表明，伴随着组织的变化，织构的类型也由形变织构变为典型的再结晶织构，且再结晶织构形成机制符合择优生长理论。
The results show that the deformation textures are turned into recrystallization textures and the mechanism of this change accords with oriented growth theory.
利用X射线衍射技术并结合金相组织观察和显微硬度实验，研究了冷轧工业纯钢在电场作用下的再结晶及织构演变规律。
The effect of electric field on the recrystallization and recrystallization texture development in cold-rolled copper was studied by X-ray diffraction (ODF analysis) combined with optical microscopy.
介绍了采用电子背散射衍射测定深冲用再结晶铌板织构的结果。
Textures in deep punching niobium sheets have been examined by the EBSD technology in the present paper.
提高终轧温度可以促进热轧板的再结晶，增加成品中有利织构组分，降低铁损，提高磁感。
High finish rolling temperature promotes the recrystallization of hot-rolled strip, increases favorable texture components, decreases the core loss, and increases magnetic induction of final product.
通过二次再结晶形成立方织构时，并不包括重新形核的过程。
It is found that cube texture in this alloy can be developed either by the process of secondary recrystallization or simply by the process of primary recrystallization.
分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。
The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.
分析了退火对热成形组织及织构的影响，确定了< 110 0 >织构的消失与残余形变晶粒再结晶的联系。
The vanishing of texture during annealing was related with the recrystallization in deformed elongate grains which survived the hot extrusion.