各种织物必须经过拉伸强力试验才能确定产品力学性能。
The mechanic property of fabric can only be determined by pulling strength test.
在压机内冷却的方式比自然冷却方式制成的复合材料空隙率低、结晶度高、拉伸强力大。
The composites cooled inside the hot-press machine has lower void content and higher crystallinity and tensile strength than that in the nature-cooling condit…
扫描电镜观察和DSC测试表明,此时的纤维表面上出现过量的TPP结晶,拉伸强力下降了70%。
The scanning electron micrograph and DSC data show that an excessive amount of TPP crystallization was on the surfaces of polylactide fibers and the tensile strength was cut down by 70%.
作者用国产单纤维电子强力仪对兔毛、澳毛和国毛进行一次拉伸试验。
The strength of rabbit hair and Australian wool was measured in one-process by means of the domestic-made single fibre strength tester.
选择适当的温度和拉伸比进行热定形,可提高PTT织物的断裂强力和弹性回复率,但其延伸性变差。
The breaking strength and resilient-elasticity recovery of PTT fabric can be increased under suitable temperature and drawing ratio during heat setting, but its dilatability took worse.
本文还研究得出柔性复合材料撕裂强力和拉伸断裂强力之间具有一致性关系。
We also studied the linear relationship between the tensile and tear performance of the flexible composites.
PTT与大豆蛋白纤维交织可以提高织物的断裂强力和拉伸回复率;
As to the fabric interlaced with PTT, it has less shrinkage, which decrease with the increasing of content of PTT.
发现处理后的复合材料的拉伸强度和剥离强力有所改善,但效果不显著。
It turned out that, the tensile and peeling properties of treated composites were better while the effect was not obvious.
在侧拉伸部分:以强力拉伸带来加长训练者的耗时性达到韧带拉伸训练肌肉的目的。
Side stretch: to lengthen the trainee's durability by big force stretch belt as to stretch the muscle with the ligament.
本文介绍了LFY-25型织物强力机自动控制织物断裂拉伸时间的方法。
The measures for controlling the breaking time on fabric strength. testing machine typeLFY-25 is introduced in this article.
用于织物的抗拉伸断裂强力及断裂伸长的测定。
Model YG 026T Electronic Table Fabric Strength Tester is used for testing the breaking strength and breaking elongation.
用于织物的抗拉伸断裂强力及断裂伸长的测定。
Model YG 026T Electronic Table Fabric Strength Tester is used for testing the breaking strength and breaking elongation.