德国研究矿渣硅酸盐水泥比普通硅酸盐水泥的信息比。
German study of slag Portland cement than Portland cement information than the.
通过大量试验探索B型矿渣硅酸盐水泥生产工艺和水泥性能，确定合理的生产控制参数。
Through many experiments, processing techniques and properties of B-type slag silicate cement was explored, and proper process control parameters were also determined.
大体积混凝土施工时常选用水泥水化热较低的矿渣硅酸盐水泥等以利于混凝土温升控制。
For massive concrete construction, the low hydration heat cement like the slag Portland cement is often used to facilitate temperature rise control in the concrete.
通过选用柠檬酸、白糖、葡萄糖酸钠为矿渣硅酸盐水泥的缓凝剂，测定了不同温度下水泥的凝结时间，分析了温度对混凝土缓凝剂最优掺量的影响规律。
The cement setting time at different temperatures has been measured through choosing citric acid, sugar and sodium gluconate as the retarders of iron Portland cement.
按新配制的活化剂生产32.5级的矿渣硅酸盐水泥、粉煤灰硅酸盐水泥和复合硅酸盐水泥，进行了成本计算，生产每吨水泥分别可获利4.85元、3.75元和22.97元。
The cost of activated grade 32.5 slag silicate cement, fly ash cement and compound cement is calculated. We can gain profits of 4. 85 yuan, 3. 75 yuan, and 22. 97 yuan each ton.
耐化学腐蚀试验表明新型碱矿渣水泥具有比普通硅酸盐水泥更优的抗化学侵蚀性；
Test results on resistance to chemical attack indicate that NASC possesses more excellent anti-chemical attacking property than that of Ordinary Portland Cement.
采用分别粉磨再混合的方式，利用正交试验方法，研究了熟料、矿渣及粉煤灰的不同细度组合对复合硅酸盐水泥物理性能的影响。
The properties of the composite cement were studied by orthogonal test, which was prepared by the clinker, slag and fly ash with different fineness and mixed after separately grinding.
研究了转炉钢渣粉对矿渣粉-硅酸盐水泥混合胶砂硬化体收缩特性的影响。
The effect of converter steel slag powder(CSSP), on the shrinkage characteristic of hardened GGBFS-PC mixed mortar is studied.
通过电镜分析研究了掺入矿渣、普通硅酸盐水泥等物质对石膏基复合材料结构性能的影响；
The influences of adding addition agent, such as slag and cement, on the microstructure and properties of gypsum composites were investigated by means of SEM analyses.
用足够细的磨细钢渣粉可以制成525普通硅酸盐水泥、525复合硅酸盐水泥、425复合硅酸盐水泥和钢渣矿渣水泥。
525and 425 ordinary Portland cement, 525 composite Portland cement, 425 steel slag Portland cement can be produced with the addition of pulverized steel slag with enough fineness.
用足够细的磨细钢渣粉可以制成525普通硅酸盐水泥、525复合硅酸盐水泥、425复合硅酸盐水泥和钢渣矿渣水泥。
525and 425 ordinary Portland cement, 525 composite Portland cement, 425 steel slag Portland cement can be produced with the addition of pulverized steel slag with enough fineness.