将废旧腈纶用常压碱法水解，用n羟甲基丙烯酰胺作交联剂制备高吸水性树脂。
High water-absorbent resin has been prepared using the useless acrylic fibres alkaline hydrolysis under the normal pressure, using the N-hydroxymethyl propylene acryl amine as the crosslinked agent.
确定最佳交联反应工艺条件为：n羟甲基丙烯酰胺与丙烯腈单体的摩尔比为0。
It is shown that the best crosslinking reaction technological condition is: the molar ratio for the N-hydroxymethyl propylene acryl amine and the acrylonitrile monomer is 0.
该粘合剂一改以往自交联反应单体采用羟甲基丙烯酰胺，使粘合剂游离甲醛超标的弊端。
While conventional adhesive will cause free formaldehyde because of using another self-crosslinking reactive monomer methylol acrylamide.
采用低毒的N羟甲基丙烯酰胺体系凝胶注模成型氧化铝陶瓷，研究了该体系下浓悬浮体的制备及固化过程。
The alumina ceramics is gel-mould cast with low toxic N methylolacrylamide system. This paper reports the investigation on the preparation of alumina suspension and its solidification process.
结果表明，当共聚单体N羟甲基丙烯酰胺（NMA）和甲基丙烯酸羟乙酯（HEMA）的质量分数分别为6%和15%时，树脂的交联度较高；
The results show that high cross-linking degree of resin can be gained as the mass fraction of comonomer N-hydroxymethyl acrylamide (NMA)and hydroxyethacrylate (HEMA)are 6% and 15% respectively.
结果表明，当共聚单体N羟甲基丙烯酰胺（NMA）和甲基丙烯酸羟乙酯（HEMA）的质量分数分别为6%和15%时，树脂的交联度较高；
The results show that high cross-linking degree of resin can be gained as the mass fraction of comonomer N-hydroxymethyl acrylamide (NMA)and hydroxyethacrylate (HEMA)are 6% and 15% respectively.