洛氏硬度（Rockwell hardness）是美国人洛克维尔于 1919 年提出。试验方法是用一个顶角为 120 度的金刚石圆锥体或直径 为 1.59mm/3.18mm 的钢球，在一定载荷下压...
基于2929个网页-相关网页
洛氏硬度计 Rockwell hardness tester ; Rockwell apparatus ; EXPORTR ; Rockwell hardometer
洛氏硬度试验 [力] Rockwell hardness test ; Rockwell Test ; Rockwell hardness ; rockweel hardness test
洛氏硬度值 [力] Rockwell hardness number
洛氏硬度试验机 Rockwell hardness tester ; Diamond Cone superficial hardness tester
洛氏硬度压头 Rockwell hardness penetrator ; Rockwell hardness indenter
表面洛氏硬度计 Rockwell superficial hardness tester
表面洛氏硬度值 Rockwell superficial hardness number
洛氏硬度B级 RB Rockwell Hardness B Scale ; RB
洛氏硬度A级 RA Rockwell Hardness A Scale ; RA
扫描电镜观察表面金刚石形貌，洛氏硬度压痕法评价涂层结合情况。
Adhesion strength of diamond films on cemented carbide were evaluated by Rockwell indentation tests.
测试了真空烧结和低压烧结试样的抗弯强度、洛氏硬度、磁饱和度和矫顽磁力。
Transverse rupture strength, Rockwell a hardness, magnetic saturation induction and magnetic coercivity of samples sintered in vacuum or by sinter-HIP were measured.
结果表明，高珠光体含量球铁凸轮轴的洛氏硬度随着球化率和珠光体含量的升高而增加。
The result showed that the Rockwell hardness of the high pearlite-containing nodular iron camshaft increased with increasing of its nodularity and pearlite content.
洛氏硬度是以压痕塑性变形深度来确定硬度值的指标，以0.002毫米作为一个硬度单位。在洛氏硬度试验中采用不同的压头和不同的试验力，会产生不同的组合，对应于洛氏硬度不同的标尺。常用的有3个标尺，其应用涵盖了几乎所有常用的金属材料。 洛氏硬度（HRC）测试，当被测样品过小或者布氏硬度（HB）大于450时，就改用洛氏硬度计量。试验方法是用一个顶角为120度的金刚石圆锥体或直径为1.5875mm/3.175mm/ 6.35mm/12.7mm的钢球，在一定载荷下压入被测材料表面，由压痕深度求出材料的硬度。最常用的三种标尺为A、B、C，即HRA、HRB、HRC，要根据实验材料硬度的不同，选用不同硬度范围的标尺来表示： HRA是采用60Kg载荷和钻石锥压入器求得的硬度，用于硬度较高的材料。例如：钢材薄板、硬质合金。 HRB 是采用100Kg载荷和直径1.5875mm淬硬的钢球求得的硬度，用于硬度较低的材料。例如：软钢、有色金属、退火钢等。 HRC 是采用150Kg载荷和钻石锥压入器求得的硬度，用于硬度较高的材料。例如：淬火钢、铸铁等。
应用推荐