Shrinkage and shrinkage porosity, stress and deformation often occurs during the production of heavy steel casting.
大型铸钢件在实际生产中易产生缩孔缩松、应力变形等缺陷。
It is discussed that adiabatic material, as well as ratio of height and width effected solidification, shrinkage cavity and shrinkage porosity.
讨论了锭模的高宽比、绝热板材质对凝固位置及缩孔疏松的影响。
According to the simulated temperature fields and solid fraction, the hot spot and shrinkage porosity are not found in the bolster casting, so the new casting process is feasible.
温度场和固相分数的模拟结果表明,铸件没有产生热节和缩孔缺陷,表明了新工艺的可行性。