Relatively low ordering temperature for the multilayer is due to the extra driving force of ordering process caused by the vanishing of the multilayer interface at annealing.
多层膜化促进有序化在较低的温度下进行,这是由于热处理过程中多层膜界面的消失提供了有序化过程额外的驱动力。
The experimental results show that the ratio of the bar-like defects to the point-like ones decreases with increase in time of nucleation annealing at a low temperature.
实验结果表明,棒状缺陷和点状缺陷的数量比随低温成核退火时间的增加而减小;对于相同的成核时间,棒状缺陷和点状缺陷的比随成核温度增加开始上升,后来下降。
A method of annealing for a long time at low temperature can be used to improve the plasticity and make the products acceptable.
提出用低温长时间退火的方法改善其塑性,通过试验确定了退火工艺制度,使产品的变形性能达到了使用要求。