Comparing the mechanical properties of Mg-4.2Zn-0.8Y alloy of T4 and T6 heat treatment with those of the as-cast condition, the tensile strength is improved by 17.2 and 37.7%, respectively, and the yield strength by 88.5 and 107.2%, respectively.2.
结果显示,热处理能够有效的提高合金的综合力学性能, T4和T6处理态Mg-4.2Zn-0.8Y合金与铸态相比,抗拉强度分别提高17.2%和37.7%;屈服强度分别提高88.5%和107.2%。
参考来源 - Mg·2,447,543篇论文数据，部分数据来源于NoteExpress
The as-cast bainite steel studied in this paper could obtain bainite directly in the as-cast condition through alloying and controlling the cast cooling rate without heat treatment.
所研究的铸态贝氏体钢是通过合金化和控制冷却速度的方法在铸态下直接得到贝氏体组织的，不需热处理即可获得所需的组织和性能。
A new production process was developed through finite element simulation. The microstructure and mechanical properties of grates at both heat treatment and as-cast condition were analyzed.
通过有限元模拟改进了原炉排制造工艺，对新工艺制造的炉排件进行取样并分析了铸态和热处理前后的显微组织和力学性能。