Theshrinkage of green body was 0.3% and the density deviation was 0.32%. After infiltrated with molten silicon, the shrinkage of sintering body had another 0.2%.
成型坯体的干燥收缩率小于0.3%,密度分布的标准偏差为0.32%,反应烧结过程中,坯体的收缩率小于0.2%。
With the increase of solids loading, the particle density increases and the bending strength of green body decreases for the network polymer accounting for only a small amount of the composition.
随着固相体积分数的增加,单位面积的颗粒分布密度增大,网络高分子在成分中只占少量,坯体抗弯强度降低。
For the green body containing a certain size of SiC powders, the carbon particle should be less than a certain size, or else, the density and fracture strength of RBSC decrease wit...
对于一定粒度的碳化硅粉而言,加入到生坯中碳粉粒度应小于一定尺寸,否则,陶瓷的断裂强度和密度将随碳粉粒度的增大而降低。