electroless plating of ni-p alloy 化学镀ni
electroless ni p alloy plating 化学镀nip合金
electroless Ni-P alloy plating 化学镀镍磷合金
Electroless plating Ni-P alloy coating after heat treatment had smaller coefficient of friction and better anti-wear ability than Cr12MoV steel after heat treatment. The experiment results showed the wear volume of the coating was one thirteenth of Cr12MoV steel.
热处理的Cr12MoV化学镀镍磷镀层与Cr12MoV相比具有较低的摩擦系数和较好的耐磨性能,在相同实验条件下,化学镀镍磷镀层的磨损体积为Cr12MoV磨损体积的1/13。
参考来源 - Cr12MoV化学镀镍—磷工艺及镀层性能研究·2,447,543篇论文数据，部分数据来源于NoteExpress
The behaviours of the initial depositing stage of electroless Ni-Co-P alloy plating on nickel and carbon steel by special sample preparation methods and TEM was studied.
摘 要： 用特殊制样手段在TEM上直接观察镍钴磷合金化学沉积的初期形貌。
Research on Pore Sealing of Electroless Ni-P Plating Alloy Covered with Silane Film;
本研究采用包埋法制备涂层并进行封闭处理。