The elongation at break and tensile strength of solvent-type epoxy modified asphalt reach 158% and 4.9MPa by the composite toughener.
通过增韧剂的复合增韧,使溶剂型环氧沥青的断裂伸长率达到158%,拉伸强度4.9MPa。
参考来源 - 环氧改性沥青的制备与性能研究·2,447,543篇论文数据，部分数据来源于NoteExpress
Through performance research of FYT, SBS modified bitumen and epoxy asphalt, shearing stress, drawing stress and aging performance of three water proofing and adhesion material have been compared.
通过对SBS改性沥青、环氧沥青、FYT桥面二涂防水粘结材料三种防水粘结材料的性能研究，对比了三种防水粘结材料的剪切强度、拉拔强度和老化性能。
Adhesive layer materials for different conditions may be recommended by using of direct shear test and pullout test with SBR modified emulsion asphalt, SBS modified asphalt and Japan epoxy binder.
采用SBR改性乳化沥青、SBS改性沥青和日本环氧粘结剂三种层间粘结剂，利用直剪试验和拉拔试验进行层间抗剪性能分析，可以推荐出适合不同条件的粘结层材料。
Water stability of asphalt mixtures modified by epoxy resin was also validated using relevant tests.
本文还选用有关试验方法，验证了环氧沥青混合料抗水损坏能力。