... 吸热峰endothermic peak 放热峰exothermic peak 注:根据热力学的惯例，当反应或转变是放热时，熔变为负。吸热时，焙变为正。吸热或放热的方向，通常在DSC ...
基于462个网页-相关网页
The curing temperature of UF decreased under the condition of curing agent according to the exothermic peak dropped from 115℃to 90℃on the DSC curve when ammonium chloride was added to UF.
在改性树脂中加入氯化铵后,树脂DSC较大的放热峰从115℃下移至90℃左右,说明在固化剂的作用下,树脂的固化温度降低。
参考来源 - 低温固化低毒脲醛树脂胶的研制·2,447,543篇论文数据，部分数据来源于NoteExpress
The activation energy obtained from the IF peak is equal to that obtained from exothermic peak of DSC.
另外，多个扫描速度所求出的DSC曲线上的晶化放热峰的表观激活能和内耗峰的表观激活能几乎完全一致。
SC-1067 for curing exothermic peak at the low shrinkage rate of new small unsaturated polyester resin.
SC -1067为固化时放热峰低、收缩率小的新型不饱和聚酯树脂。
HCH-6993 for a curing exothermic peak at the low shrinkage rate of new small unsaturated polyester resin.
6993为固化时放热峰低、收缩率小的新型不饱和聚酯树脂。