The main crystalline phase of the membranes is anatase;The aperture range is approximately from 30nm to 150nm and average aperture is about 70～80nm.
其主晶相是锐钛矿型,孔径分布为30～150nm,平均孔径在70～80nm之间。
参考来源 - 二氧化钛担载分离膜的制备工艺研究·2,447,543篇论文数据，部分数据来源于NoteExpress
The XRD result shows that the main crystalline phase of the ceramic is mullite.
射线衍射分析结果表明，材料的主晶相为莫来石。
Y2O3 has obvious influence on the microstructure, however, it doesn't change the main crystalline phase of the glass-ceramics.
Y2O3的加入并不影响微晶玻璃中主晶相的组成，但对其微观结构有明显影响；
Caloivm Aluminum Oxide and Clinoenstatite Syn as main Crystalline phase with the addition of slag and glass powder more than 70 percent in minor ingredients.
该材料以镁方柱石、铝酸三钙、斜顽辉石为主晶相，配料中矿渣和玻璃粉用量高于70%。