The result shows improving complex sample's temperature is good to gain metallurgical bonding interface.
实验结果表明:提高浇注时复合试样的整体温度有利于获得界面的冶金结合。
The interface layer of metallurgical bonding will not induce brittle fracture and will share the ductile SEM fractographs of the substrate.
这种界面冶金结合层并不会引起脆性断裂,具有与基材相同的韧性断口形貌。