再结晶退火（recrystallization annealing）：经冷加工的钢丝加热到再结晶温度以上、Ac1 点以下，保温 适当时间，然后空冷，使晶粒重新结晶为均匀的等轴晶粒，以消除冷加工硬...
基于533个网页-相关网页
The simulation researches and the experiments of annealing processes of ELC-BH steel plate and commercial pure aluminum (1060) plate are carried out, respectively. The results verify the rationality of the recrystallization annealing model for textural materials.
且分别针对冷轧ELC-BH钢板及1060(L2)工业纯铝板进行了退火实验和模拟研究,证实了该模型是合理的且较好地模拟了实际变形织构材料的再结晶退火过程组织演变。
参考来源 - 织构材料再结晶退火的蒙特卡罗模型及其模拟研究·2,447,543篇论文数据，部分数据来源于NoteExpress
The different recrystallization annealing temperature and the micro-hardness of sample show the complex relationship.
不同的再结晶退火温度与试样的显微硬度表现出复杂关系。
The microstructure and hardness of T2 copper subjected to stamping deformation at 77 K and subsequently recrystallization annealing were studied.
研究了工业纯铜T2在77 K温度下快速压缩变形的组织变化和再结晶退火温度、时间对其组织、性能的影响。
In this paper, the copper sheets were subject to asymmetrical accumulative rolling-bonding (AARB) by different passes and recrystallization annealing.
本论文选用工业纯铜板材作为研究对象，对其进行了不同道次的异步叠轧和再结晶退火实验。