The morphology of austenite dendrites in shrinkage porosity in nodular iron is displayed by the color etching technique and the formation mechanism of shrinkage porosity has been analyzed.
采用着色腐蚀技术,金相显示了球墨铸铁缩松区中奥氏体枝晶组织形貌,分析了球铁缩松的形成机制。
Large thick-section ductile Iron housing easily produces casting defects such as shrinkage cavity, shrinkage porosity, graphite floating and spheroidizing decay.
大型厚断面球墨铸铁件在铸造过程中极易产生缩孔、缩松、石墨漂浮及球化衰退等铸造缺陷。
The influence of chemical composition, inoculation process, temperature of molten iron and pouring system on the formation of shrinkage cavity and porosity was described.
叙述化学成分、孕育工艺、铁液温度及浇注系统等因素对薄壁球铁铸件缩孔和缩松形成的影响。