By using this combination of process parameter, can reduce the defects such as gas trapping, oxide inclusion, shrinkage cavity and porosity, and shorten the production cycle of casting.
此组参数可减少裹气、氧化夹杂、缩松缩孔等铸造缺陷,并缩短压铸单位生产周期。
参考来源 - 汽车铝合金轮毂压铸过程数值模拟及工艺参数优化·2,447,543篇论文数据,部分数据来源于NoteExpress
The main task of this paper is to develop prediction & analysis system of shrinkage cavity and porosity defect in a casting for foundry engineering application.
本论文以有限元分析软件为开发平台,运用设计参数化和功能模块化技术,初步开发了面向铸造工程应用的铸件缩孔缩松预测及缺陷分析系统。
Batch production shows there are no shrinkage cavity and porosity in casting, and no blowholes and sand inclusions on the top surface. The yield of the casting is 81%.
经批量生产验证,铸件内无缩孔、缩松缺陷,上表面无渣孔、气孔缺陷,工艺出品率81%。
The influence of chemical composition, inoculation process, temperature of molten iron and pouring system on the formation of shrinkage cavity and porosity was described.
叙述化学成分、孕育工艺、铁液温度及浇注系统等因素对薄壁球铁铸件缩孔和缩松形成的影响。