文章详细信息 关键词： 蠕墨铸铁;;REMgTiSiFe合金;;铸造性能 [gap=344]Keywords: vermicular graphite cast iron;REMgTiSiFe alloy;casting property
基于72个网页-相关网页
The results show that when the ratio of V/Ti is 1.63,the vermicular graphite cast iron has a more uniform structure of ferrite matrix+vermicular graphite,and good thermal properties.
结果表明,在V、Ti变化范围内,V/Ti比为1.63时蠕墨铸铁具有较均匀的铁素体基体+蠕虫状石墨组织,以及良好的热物性。
参考来源 - V、Ti合金化对玻璃模具材料抗氧化及耐热疲劳性的影响·2,447,543篇论文数据，部分数据来源于NoteExpress
The reasons of low percentage elongation of mid Si Mo vermicular graphite cast iron exhaust tube casting in trial production were analyzed.
对试生产的中硅钼合金蠕墨铸铁排气管铸件本体伸长率不足的原因进行了显微组织分析。
The ductile-embrittlement transition temperature of vermicular graphite cast iron increased with increasing phosphorus content both in the as-cast and annealed condition.
蠕铁的韧性——脆性转变温度铸态和退火态均随磷含量的增加而升高。