结果表示 概述 维卡软化温度(Vicat softening temperature)是评 价热塑性塑料高温变形趋势的一种方法,它是在 选定的均匀升温速率下和规定的负载下,使截面 积为1mm2的圆柱状平头针压入热塑性...
基于102个网页-相关网页
维卡软点温度（Vicat Softening Temperature） 也叫维卡软化点， 是评价塑料高温变形趋势的一种方法。 是在等速升温条件下， 用一根带有规当平顶针刺入试样 1mm 时的温度， 即...
基于22个网页-相关网页
Polyvinyl chloride (PVC)/styrene-maleic anhydride copolymer (SMAH) blends were studied. The effects of the types and loading of SMAH on the notched Izod impact strength (IS), melt flow index (MFR) and Vicat softening temperature (VST) were investigated.
研究了聚氯乙烯(PVC)与(苯乙烯/马来酸酐)共聚物(SMAH)的共混改性,测定了共混物的冲击强度、熔体流动速率和维卡软化点。
参考来源 - PVC/SMAH共混物的研究·2,447,543篇论文数据，部分数据来源于NoteExpress
The result showed that the tensile strength property and Vicat softening temperature was increased and notched impact property of PVC/ABS composite was decreased with the glass fiber added.
研究结果表明：随着玻璃纤维添加份数的增加，PVC/ABS合金的拉伸性能和维卡软化温度有不同程度的提高，缺口冲击强度有所下降。
The results showed that the glass transition temperature and vicat softening point increased obviously with the increase of the content of the terpolymer.
结果表明：随共聚物用量的增加，共混物的玻璃化温度和维卡软化点明显提高；