The tensile strength, elongation and hardness of T10 steel subjected to magnetic field quenching and to high temperature tempering were separately increased by 28%, by 8.
与经普通淬火和高温回火的相比，经磁场淬火和高温回火的T10钢的抗拉强度提高了28%，断后伸长率提高了8。
The test results show that the surface of H13 steel can obtain the optimum performance at temperature of complete annealing, quenching and tempering.
试验结果表明H13钢在最佳完全退火温度、淬火温度、回火温度下可得到最优综合性能。
Its CCT curve was determined by test. The influence of quenching and tempering temperature on the mechanical properties was also studied.
试验测定了该钢的CCT曲线，探讨了淬火和回火加热温度对该钢力学性能的影响。