...成型； 固相体积分数； 粘度[gap=1368]Key words: PTCR chip thermistors; multilayered structure; gelcasting; solids loading; viscosity...
基于24个网页-相关网页
By using these methods, the viscosity of suspension was less than 0.32Pa. s and green strength was up to 32MPa, which made it possible to machine. Through adjusting the particle distribution the solids loading amounted to 54vol%.
并通过调整粉料的颗粒级配,使悬浮体固相体积分数达到54vol%。
参考来源 - SialonAs the solid content in suspension increased,the density of FGMs increased,but the composition gradient decreased.
随固相体积分数的增加,样品致密度逐渐增大,而成分梯度逐渐降低。
参考来源 - 组元磁化法制备ZrO·2,447,543篇论文数据，部分数据来源于NoteExpress
随固相体积分数的增加，水基凝胶注模法坯体密度逐渐增加，但强度逐渐降低。
With increasing solid loading, density of AGC green body increases gradually, but strength decreases gradually.
随着固相体积分数的增加，单位面积的颗粒分布密度增大，网络高分子在成分中只占少量，坯体抗弯强度降低。
With the increase of solids loading, the particle density increases and the bending strength of green body decreases for the network polymer accounting for only a small amount of the composition.