常温耐压强度是指制品在室温下测得的数值;将试样加热至某一指定温度进行加压试验，所取得的结果称为该温度下高温耐压强度。制品耐压强度的高低主要取决于自身的材质类别，但制造工艺水平对耐压强度值有很大影响。
... 显气孔率/Apparent Porosity ％ 常温耐压强度/Cold crushing strength MPa 热震稳定性次数/Thermal shock resistance ...
基于36个网页-相关网页
... 涂料 coating 常温耐压强度 cold compressive strength 稠度 consistency ...
基于18个网页-相关网页
... 抗弯强度 flexure strength 常温耐压强度Ambient compressive strength 常温抗折强度Cold bending strength (Mpa) ≥ ...
基于15个网页-相关网页
常温耐压强度试验方法 Determination of cold compressive strength
讨论了气孔率、体积密度和常温耐压强度与电熔氧化镁加入量之间的关系。
The porosity, bulk density and cold crushing strength of the refractory samples were determined.
试验结果表明，在配料中加入适量混合稀土氧化物对提高耐火制品的常温耐压强度和热震稳定性能是有益的。
The results show that a certain amount of the mixed rare earth oxide content in the batch can increase the cold compression strength and the thermal shock resistance of the bricks.
制得高强度耐火粘土砖的试验结果表明：浸渍处理后的试样，常温耐压强度均获得了不同程度的提高，体积密度增加，气孔率下降。
The result shows that the compressive strength at normal temperature of impregnated samples is raised in varying degree, their bulk density is increased and the porosity is decreased.