The complex of super water absorbing resin-natural fabric were obtained by microwave radiation polymerization of natural fabric which dip-coated in acrylic acid and its sodium salt aqueous solution.
将含聚合引发剂的丙烯酸盐单体水溶液涂布到天然纤维布基材上，在微波辐照下聚合，制得高吸水性纤维复合体。
This paper described a pilot process of polymerization of acrylamide in middle concentration (30 ~ 35% by weight) aqueous solution with the additive disodium EDTA.
本文叙述了丙烯酰胺辐射聚合中间试验。采用中等浓度丙烯酰胺水溶液(30—35%按重量)，加入添加剂EDTA二钠。
The polymerization of acrylonitrile in aqueous nitric acid solution with sodium nitrite as initiator has been studied.
研究了亚硝酸钠引发硝酸溶液中丙烯腈的聚合反应。
The dispersion polymerization of water soluble monomers in aqueous solution is a new kind of green synthesis technology.
水溶性单体在盐水介质中的分散聚合是一种新型绿色合成技术。
The kinetics of polymerization of acrylamide in aqueous solution induced by ammonium persulphate-sodium bisulfite-ammonium bicarbonate is studied and a kinetic equation is therefore obtained.
研究了过硫酸铵—亚硫酸氢钠—碳酸氢铵引发下丙烯酰胺水溶液聚合的动力学，导出了聚合动力学方程。
The influence of polymerization conditions on conversion and intrinsic viscosity of polymer were investigated. The rheological properties in an aqueous solution were also studied.
研究了聚合条件对聚合物产率及特性粘度的影响，并研究了聚合物水溶液的流变性能。
The suspension polymerization of DMAHPMA has been carried out easily and successfully in 10% NaCl aqueous solution without any addition of suspension stabilizers.
DMAHPMA在10％的盐水溶液中，不加悬浮稳定剂，即能成功地进行悬浮聚合。
Aqueous polyacrylic size was synthesized by solution or emulsion polymerization, then, the resultant product was converted into the powdery size through sedimentation, drying, and crush break.
通过溶液聚合法、乳液聚合法合成了聚丙烯酸液体浆料，对所合成的聚丙烯酸液体浆料经沉降、烘干、粉碎制取了粉体聚丙烯酸浆料。
Aqueous polyacrylic size was synthesized by solution or emulsion polymerization, then, the resultant product was converted into the powdery size through sedimentation, drying, and crush break.
通过溶液聚合法、乳液聚合法合成了聚丙烯酸液体浆料，对所合成的聚丙烯酸液体浆料经沉降、烘干、粉碎制取了粉体聚丙烯酸浆料。