黄铜表面在氨水中腐蚀或应力腐蚀时形成脱锌层，由此产生一个附加拉应力。
Dezincification layer is formed on brass during corrosion or stress corrosion cracking (SCC) in ammonia solution, and an additive stress is induced in the same time.