The mechanism of SCC is an anodic dissolution with film rupture rate-controlling.
应力腐蚀破裂机制为膜破裂控制的阳极溶解。
Anode slime: in the current under the action of the residue after an anodic dissolution.
阳极泥：在电流作用下阳极溶解后的残留物。
The creep rate was increased while the yield strength was reduced by anodic dissolution.
阳极电流不但使恒载荷下的不锈钢蠕变速度增加，而且使屈服强度下降。
At the same cathodic polarization potential, the anodic dissolution current of the B was smaller thanA and c.
在同样的阴极极化电位下，B钢的阳极溶解电流也明显小于后两者。
The inhibitive effect resulted from inhibiting the anodic dissolution and the cathodic reaction of aluminium alloy.
钼酸铵主要是通过抑制铝合金的阴极反应和阳极溶解来达到缓蚀作用的。
On the different stages of crack growth, the relative contribution of interaction between hydrogen and anodic dissolution is different.
在裂纹扩展不同阶段氢和阳极溶解交互作用相对贡献大小不同。
The potentiostat is one of the principal instruments used to control an anodic dissolution process accurately in electrochemical experiments.
恒电位仪是在合金相电解提取中精确控制阳极溶解过租的重要仪器。
As the ion contents of the soil simulation solution doubled, the anodic dissolution of degenerated pearlite increases, and the local impedance of the electrode decreases.
模拟溶液各离子含量成倍增加后，退化珠光体的阳极电流密度升高，电化学交流阻抗值降低，局部腐蚀效应增大。
At lower anodic potential and OCP, anodic dissolution is weak. The difference of dissolution between crack tip and other surfaces exist. These facts benefit the crack propagation.
阳极电位较弱以及开路电位下，阳极溶解较弱，裂尖和其他表面存在溶解性差异，这些因素有利于裂纹扩展。
T73 and RRA treatment improve the grain boundary character, which is help to inhibit hydrogen embrittlement and decrease anodic dissolution rate, then to improve the SCCR of the alloy.
T73和RRA时效处理改善了合金晶界特性，有助于阻止氢脆、减缓晶界阳极溶解速度，提高合金的抗应力腐蚀能力。
This indicates that normal stress component plays a dominant role in stress corrosion of this system, which is related to the anodic dissolution accelerated by normal stress component.
这表明，正应力在这种应力腐蚀体系中起主导作用，这和正应力能促进阳极溶解过程有关。
Ellipsometry, A. C. impedance and potential measurements have been used to study the dissolution behaviour and corrosion resistance of titanium anodic oxide film in 0.5n sulfuric acid.
本文用椭园法、交流阻抗及电位测量研究了钛阳极氧化膜在0.5N硫酸中的溶解规律和耐蚀性。
However, at more anodic potentials another dissolution process was observed producing noticeable changes on the surface morphology which could be ascribed to the dissolution of a au-sn surface alloy.
然而，在另一个阳极电位更正的阳极溶解过程中，观察到在表面形貌上产生明显变化的原因是金锡合金的溶解。
Dissolution of zinc and low carbon steel anodes and anodic polarization behaviors thereof were studied.
研究了锌和低碳钢阳极在碱性锌镍合金镀液中的溶解特性及阳极极化行为。
Dissolution of zinc and low carbon steel anodes and anodic polarization behaviors thereof were studied.
研究了锌和低碳钢阳极在碱性锌镍合金镀液中的溶解特性及阳极极化行为。