The unsuitable carbonitriding process, internal oxidation, over deep depth of carbonitrided layer and crust like C N compound on the surface are the main reasons to cause fracture.
碳氮共渗工艺选择不当，共渗层过深，表面出现壳状碳氮化合物、内氧化等缺陷组织是造成其断裂的主要原因。
The unsuitable carbonitriding process, internal oxidation, over deep depth of carbonitrided layer and crust like C N compound on the surface are the main reasons to cause fracture.
碳氮共渗工艺选择不当，共渗层过深，表面出现壳状碳氮化合物、内氧化等缺陷组织是造成其断裂的主要原因。