Shear test of clad steel plate and sheet was carried out according to old and new standards.
按新、旧两种剪切试验标准对相同材料进行了大量试验研究。
This paper introduced the distribution and pattern of two conceal defects in explosive welding stainless clad steel plate and their ultrasonic inspection.
本文主要介绍了爆炸焊接不锈钢复合板中两种隐蔽性缺陷的形态、分布规律以及超声波检测。
The results show that martensite at transition area and the thermal stress in the joint of different material will cause crack in clad steel plate during welding.
结果表明，过渡区马氏体组织的生成，异种钢接头的热应力是产生焊接裂纹的主要原因。
Aiming at the fairly disadvantages in different realizations of stainless-clad steel plate at present, a new production method-brazing and soldering rolled method is developed.
针对目前不锈钢复合板各生产方法存在的诸多不足，研制开发了钎焊轧制法。
Austenitic stainless steel including clad plate shall generally be subjected to cold forming.
奥氏体不锈钢包括包装板通常使用冷成型。
The paper analyzed the welding characteristic of stainless steel clad plate, and summarized three factors that were welding groove, welding materials and parameter, welding sequence.
对不锈钢复合钢板的焊接特点进行了理论分析，总结出其焊接三要素：焊接坡口、焊接材料和参数、焊接顺序。
The practice proved that the welding quality of stainless steel clad plate was very steady if following the welding points.
实践证明，只要遵循其焊接要点，不锈钢复合钢板的焊接质量是非常稳定的。
The present paper discusses chemical compositions, structures and properties of explosion welded and rolled Ni stainless steel clad plate after annealing treatment under different process conditions.
讨论镍—不锈钢爆炸+轧制复合板在不同工艺下退火后的成分、组织和性能，在本试验的条件下，该复合板都有良好的结果。
The existing manufacturing Technology for Clad Plate of Stainless Steel were introduced, and the advantages and disadvantages of these processes were analyzed.
阐述了目前不锈钢复合板的生产方法和制备技术，分析了各种方法的优缺点。
This paper describes the effect of hot-rolling technology on the composition, structure and properties of explosion-formed Ti-steel clad plate.
本文叙述热轧工艺对钛-钢爆炸复合板的成分、组织和性能的影响。
Vessels with integrally clad linings shall be made of plate clad with the required lining material at the steel mill in accordance with the applicable material specifications.
整体加衬里的容器根据所用的材料规格在钢厂中采用所需的加衬材料加工制成镀板。
In this article defect occurring reason was analyzed and hold that the defect was caused by the special welding structure of the stainless steel clad plate and fabrication process.
文中对缺陷产生的原因进行了分析，认为缺陷系不锈钢复合钢特殊的焊接结构和制造工艺所致。
In this article defect occurring reason was analyzed and hold that the defect was caused by the special welding structure of the stainless steel clad plate and fabrication process.
文中对缺陷产生的原因进行了分析，认为缺陷系不锈钢复合钢特殊的焊接结构和制造工艺所致。