The transformation superplasticity in welding CGHAZ (Coarse Grain Heat Affected Zone) of EH36MOD steel and its effect on fatigue life have been studied with thermal simulating method.
采用热模拟方法，对EH36MOD钢焊接热影响区粗晶区(CGHAZ)的相变超塑性及其对疲劳寿命的影响进行了研究。
Microstructure of simulated coarse grain heat affected zone (CGHAZ) of Zr Microalloyed HSLA Steel are investigated using optical microscopy and transmission electron microscopy.
采用光学显微镜和透射电镜研究了锆处理对微合金钢粗晶热影响区组织的影响。
The coarse grain zones of laser welded joint of super fine grain steel show good toughness.
超细晶粒钢激光焊接接头粗晶区有较好的韧性。
The results showed that the metallurgical defects such as inclusions, coarse crystal grains and asymmetry of the grain size were the main reason resulting in fracture of the steel rods during drawing.
结果表明，原材料中存在的夹杂物、晶粒粗大及混晶等冶金质量缺陷是盘条在拉拔过程中发生断裂的主要原因。
Owing to heat action during X80 pipeline steel welding the organization and performance of heat affected zone will change considerably in particular of coarse grain heat affected zone (CGHAZ).
X80管线钢在焊接过程中，热影响区由于受到焊接过程热的作用，其组织和性能会发生较大的变化，尤其是粗晶热影响区的组织和性能变化最大。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone (HAZ) near bond line in welded joint was low. The reason is coarse grain in HAZ.
在TCS不锈钢前期焊接试验中发现其焊接接头热影响区的冲击吸收功值在熔合线附近较低，原因是接头热影响区晶粒粗大所致。
The results show that the coarse austenite grain in heat affect zone (HAZ) of Ni-base alloy is observed, mass ferrite appears in HAZ of X60 steel.
高温高压法加速腐蚀。结果表明，C4镍基合金热影响区奥氏体晶粒长大，X60钢过热区为大块铁素体组织。
The results show that the coarse austenite grain in heat affect zone (HAZ) of Ni-base alloy is observed, mass ferrite appears in HAZ of X60 steel.
高温高压法加速腐蚀。结果表明，C4镍基合金热影响区奥氏体晶粒长大，X60钢过热区为大块铁素体组织。