The technological process of the Al killed cold heading steel SWRCH18A in the No.
以SWRCH18A钢为例介绍了湘钢二炼钢厂含铝冷镦钢的生产工艺。
The influence of various cooling speed on structure and property of wire bar of SCM435 cold heading steel is researched.
研究了不同冷却速度对SCM 435冷镦钢盘条组织性能的影响。
Quality problems existing in finished cold heading steel are discussed and measures improving quality of cold heading steel are put forward.
探讨冷镦钢成品中所存在的质量问题，同时提出提高冷镦钢质量的措施。
Carbide Die: including cold heading steel ball mold, cutting tool material, feed tire, the production quality and stability ball mold, long life, can be comparable imported mold.
硬质合金模具：包氨基酸叶面肥括冷镦钢球模具、切料刀、料胎、所生产钢球模具质量稳定、寿命长、可以和进口蔬菜叶面肥模具相媲美。
To introduce the trial production process of ML08Al cold heading steel adopting the process of converter steel-making, LF refining, billet continuous cast and high speed wire rod mill.
介绍采用转炉、l F炉精炼、小方坯连铸机、高速线材轧机生产工艺试制ML 08 A l冷镦钢的过程。
Aim at faultiness and oneness of the appraisal method of cold heading steel, this paper has proposed the cone forging method. It proves feasibility and gives the rudiment of the method.
鉴于冷镦钢的冷镦性能评价方法的单一性和不完善性，提出了锥锻方法，并从理论上证明了此种检验方法的可行性。
The cold heading property of cold heading steel rod bundle is improved by the optimum design and control of chemical compositions of low carbon low silicon high aluminium cold heading steel.
通过对低碳低硅高铝冷镦钢成分的优化设计和控制，大大提高了冷镦钢盘条的冷镦性能。
The cold heading steel coil generally is low and medium carbon quality steel and alloy structure steel to manufacture various standard mechanical element and fastener by cold heading forming.
冷镦钢盘条一般为低、中碳优质碳素结构钢和优质合金结构钢，用来冷镦成型制造各种机械标准件和紧固件。
Crack is the mostly quality flaw. The facts affecting crack are analysed by testing. Then the efficient measures are taken, crack is removed, and quality of cold heading steel can be increased.
裂纹是冷镦钢的主要质量缺陷，通过检试验方法，分析裂纹成因，采取有效措施，从而消除裂纹，提高冷镦钢的质量。
These inclusions resulted in cracking of the cold forging steel during the cold heading process.
通过理化检测，对铆螺钢在冷镦时出现开裂的原因进行了分析。
Describe some questions of the national standard modification statement of steel for cold heading and cold extruding.
简述了冷镦和冷挤压用钢国家标准修订说明中的一点儿问题。
The headstand wire drawn machine is a suitable equipment for the production of heavy coil bearing steel wire for high speed cold heading.
大盘重高速冷镦机用轴承钢丝的生产，用倒立式拉丝机是比较合适的选择。
Introduction STEEL BOLTS are typically formed from rod by cold heading.
介绍钢锚杆杆通常形成了从冷的标题。
The results showed that the cold heading cracking was due to abnormal surface microstructures of steel. The abnormal surface microstructures have three kinds of behavior.
研究结果表明，目前出现的冷镦开裂是由盘条表层组织异常所致。
In this paper, typical surface defects of low carbon steel high speed wires for cold-heading have been examined by using SEM and EDS.
采用扫描电镜和能谱仪对低碳冷镦用高速线材表面缺陷进行了分析，同时对轧制中间料的缺陷和成品冷镦标准件开裂样品进行对照分析。
In this paper, typical surface defects of low carbon steel high speed wires for cold-heading have been examined by using SEM and EDS.
采用扫描电镜和能谱仪对低碳冷镦用高速线材表面缺陷进行了分析，同时对轧制中间料的缺陷和成品冷镦标准件开裂样品进行对照分析。