The results show that the crack growth rate under high-low cycle complex fatigue load is greater than that under low cycle fatigue load, and so the fatigue life is obviously reduced.
结果表明：与纯低周载荷作用相比，高低周复合载荷下球墨铸铁的裂纹扩展速率明显加快，极大地降低材料的疲劳寿命。
The fretting fatigue life under complex loads monotonously decreases with the increase of the high cycle load while the low cycle loads keep constant.
复合载荷下，低周幅值不变，增加高周载荷的幅值，微动疲劳寿命随幅值比的增加而降低。
The fretting fatigue life under complex loads monotonously decreases with the increase of the high cycle load while the low cycle loads keep constant.
复合载荷下，低周幅值不变，增加高周载荷的幅值，微动疲劳寿命随幅值比的增加而降低。