Chemical oxidation: through the chemical processing the metal surface oxidation film formation process.
化学氧化：通过化学处理使金属表面形成氧化膜的过程。
Must do derusting and to oxidation film processing, generally use chemical polishing or electrolytic polishing.
必须先做除锈及去氧化膜处理，一般使用化学抛光或电解抛光。
Peeling of oxidation film and oxidation-decarbonization are more serious on the surface than on the sub-surface.
试样表面的氧化腐蚀及氧化皮剥落均比次表层严重，表面的开裂也加速了次表层裂纹的形核和扩展。
Structure, composition and corrosion resistance of the anodic oxidation film on the magnesium alloy surface were discussed.
在硫酸电解液中加入适量由羧酸和有机化合物组成的添加剂 ，制得铝合金阳极氧化膜。
In the first stage of anodic deposition, the flocculent oxidation film deposits and extends on the surface of magnesium alloy.
阳极沉积阶段是在阳极表面形成团絮状的沉积氧化膜及氧化膜不断扩展的过程；
The effects of anodic oxidation process on thickness, corrosion resistance and surface morphology of hard oxidation film were studied.
为了研究阳极氧化工艺条件对硬质氧化膜的厚度、耐蚀性、表面形貌的影响。
According to the requirement of the mechanical properties and oxidation film of 6063 alloy, the best plan of alloy component is presented.
根据对6063合金力学性能和氧化膜的要求，提出了最佳的合金成分方案。
The heated oxidation film of U-Nb alloy is studied by auger electron spectroscopy (AES) at different temperature in the high vacuum chamber.
用俄歇电子能谱（AES）研究了高真空下，环境温度对铀铌合金真空氧化膜的影响。
The influences of electrolyte components and preparation parameters on the film-forming process as well as properties of oxidation film were discussed.
对电解液中的各组分在成膜过程中的作用及电解工艺参数对成膜过程和膜层性能的影响进行了研究探讨。
Black oxidation film on aluminum alloy with good adhension, strong corrosion resistance and beautiful color can be obtained by two steps of oxidation coloring.
阶梯形铝器皿有二个优点：一是增加器皿的刚度； 二是经过阳极氧化着色之后阶梯越多越美观。
In a given anodic oxidation condition, a hard anodic oxidation film can be obtained on the surface of aluminum - matrix composite with an excellent anticorrosion.
在适当阳极氧化工艺条件下，颗粒增强铝基复合材料表面可以制得优良耐蚀性的硬质阳极氧化膜。
Weak erosion before plating, in a certain: remove metal parts in the solution of surface extremely thin oxidation film, and make the process of surface activation.
弱浸蚀：电镀前，在一定组成溶液中除去金属制件表面极薄的氧化膜，并使表面活化的过程。
The influences of temperature, time and voltage on the thickness of oxidation film, aperture and order degree during anodic oxidation were studied by orthogonal test.
采用正交实验研究了阳极氧化时温度、时间、电压对氧化铝膜厚度、孔径和孔有序度的影响。
The density oxidation film is formed with ultrasonic electrodeposition, the oxidation resistance at high-temperature is superior to electrodeposition without ultrasonic.
有超声镀层的可形成致密的氧化膜，其高温抗氧化性能要优于无超声镀层的。
The results show that a compact oxidation film on surface of magnesium alloy can be deposited under micro-arc restrained, which is harder and more resistant to acid and alkali.
结果表明，在抑制阳极发生弧光放电的状态下，镁合金表面可以沉积一层致密的氧化厚膜层，该膜层具有较高的硬度和优良的耐蚀性能。
The main cause of better corrosion resistance was due to growth of granules, decrease of grain boundary area, and formation of thick and compact oxidation film on the coating surface.
晶粒长大、晶界面积减少以及镀层表面生成较厚的、致密的氧化膜是耐蚀性提高的主要原因。
The function of components of electrolyte in film-forming process and the influence of preparation parameters on the film-forming process and the properties of oxidation film were researched.
就电解液中各组分在成膜过程中的作用以及电解工艺参数对成膜过程和膜层性能的影响进行了研究探讨。
The melting loss has relations with size of melting bath, oxidation film property of melting charge, melting process and melting operation, etc, during melting aluminium alloy in reflecting frunace.
反射炉熔炼铝合金时，熔损与熔池几何尺寸、熔体氧化膜性质、熔炼工艺及操作等因素有关。
The sketch map of change on microstructure of anodic oxidation film during the reaming process and the process parameters for obtaining the multi-coloring by blocking layer adjusting were presented.
给出了扩孔处理过程中阳极氧化膜横断面的显微结构变化示意图，并给出了“阻挡层调整”实现多色化的工艺参数。
Material oxidation, such as oxidation spot, serious after heat treatment of oxide film.
素材氧化严重，如氧化斑，热处理后氧化膜。
As the film thickness increases with temperature and time, cracks appear and further oxidation of aluminium alloys is possible.
作为膜厚度随温度和时间、裂缝的出现和进一步氧化铝合金是可能的。
Excellent oxidation stability and cleaning performance, can effectively reduce the paint film, sediment and carbon produce.
极佳的氧化稳定性和清洗性能，能有效的减少漆膜、沉积物和积碳产生。
It is mainly reason that wet and salt spray environment and thin film of chemical oxidation.
潮湿的盐雾环境和化学氧化膜的薄而软是引起腐蚀的主要原因。
The oxidation level, the composition of the oxide film, the oxidative temperature and the relation between constituents of the alloy are clearly shown on the diagram.
在所得到的氧化图上清楚地显示了氧化水平、氧化膜的组成、氧化温度及合金成分之间的关系。
The additive and oxidation conditions can also influence the anodized film 's structure.
添加剂和氧化条件对氧化膜结构的影响也较大。
Objectives: To study the oxide film of pure titanium implant material treated by anodic oxidation .
目的：研究阳极氧化对纯钛种植材料氧化膜的影响。
By hard anode oxidation, the film is obtained when industrial pure aluminum is in sulfuric acid solution, make the improvement in the traditional sulfuric acid hard anodizing craft foundation.
对工业纯铝在硫酸溶液中采用硬质阳极氧化的方法制取氧化膜的工艺进行了研究，在传统硫酸硬质阳极氧化工艺的基础上进行了改进。
By hard anode oxidation, the film is obtained when industrial pure aluminum is in sulfuric acid solution, make the improvement in the traditional sulfuric acid hard anodizing craft foundation.
对工业纯铝在硫酸溶液中采用硬质阳极氧化的方法制取氧化膜的工艺进行了研究，在传统硫酸硬质阳极氧化工艺的基础上进行了改进。