Leading products: Hot-rolled coil, High-speed wire rod, steel billet.
主导产品为：热轧板卷、高速线材、钢坯。
Continuous casting of steel billet is a new steel-smelting technology.
板坯连铸是炼钢新工艺。
A calculation model is proposed for explosive cladding of steel billet.
提出了一个钢坯爆炸焊接的计算模型。
The oxidation resistant coatings applied to steel billet at high temperature were summarized.
概述了国内外钢坯高温防氧化涂料的研究现状。
Application status of a new homemade coating for steel billet in high temperature dynamic process was introduced.
介绍了一种自主开发的动态过程钢坯高温防氧化涂料的应用状况。
The technical requirement of oxidation resistant coatings applied to steel billet in high temperature dynamic process was analyzed.
分析了动态过程钢坯高温防氧化涂料的技术要求。
We produce and sell shaped stainless steel like stainless bars, Angle steel, channel steel, flat steel bars, steel wire, steel billet.
我厂主要生产不锈钢棒、六角棒、方棒、角钢、槽钢、钢带、扁钢、工字钢、钢丝、钢锭等异型材。
Hot-shear blade is the main tool which is used to cut hot rolling steel billet. Its performance directly affects the quality of continuous metal casting billet.
热剪刃是钢厂用来切断热轧钢坯的主要工具，其性能直接影响到连铸钢坯的质量。
However, if the effective descaling is carried out, it is very important to control the feeding speed of steel billet, the flow rate of water and the pressure of water.
但要实现有效除鳞，控制钢坯速度、水的流量及水压大小至关重要。文章介绍了高压水除鳞控制系统的结构与功能。
The hydraulic shear for square stainless steel billet designed by our company for caster is introduced, its type selection, structure and shear stress calculation are analyzed.
介绍了邢台机械轧辊（集团）有限公司设计的连铸机用不锈钢矩形坯液压平剪，对该液压剪的选型、剪力计算进行了分析。
This article analyzes the technical difficulty based on the introduction of the lossless detection on line method of the hot-rolled steel billet and sets down the corresponding countermeasure.
在对热轧钢坯在线无损检测的方法进行介绍的基础上，对技术难点做分析并制定相应的对策。
The exploratory testing study of modifying and fining the solidification structure of concast steel billet is carried out in concast production by the technology of electro-pulse modification.
在连铸生产中利用电脉冲孕育处理技术，开展改善和细化连铸坯凝固组织的试验研究。
Owing to the effect of the high temperature, complex illumination and bad-imaging environment, there are a lot of difficulties in real-time automatic character recognition at ends of steel billet.
由于高温及复杂光照的干扰等成像环境的影响，钢坯端面字符自动识别存在很多困难，其实时自动识别难度大。
The main technical parameters, work theory, technical features of walking-beam heating furnace for big square billet are analyzed simply, its utilization in Shi Steel introduced.
简要分析了石钢大方坯步进梁式加热炉的主要技术参数、工作原理、技术特点，介绍了该加热炉在石钢的应用情况。
The reformation of double duo mill and realization casting billet hot delivery and hot charging in Xinyu Iron and Steel Corp. are introduced. , and its further development is predicted.
介绍了新余钢铁有限责任公司线材厂对复二重轧机进行一火成材改造，实现连铸坯热送热装的过程，并对该厂今后的改造工程进行了预测。
The steel liquid superheat, velocity and rule of secondary cooling are important process parameters influence on billet internal quality.
钢水过热度、拉速和二冷制度是影响铸坯内部质量的重要工艺参数。
The cause for Angle crack on small billet in Chengde Iron and Steel Company is analyzed, the measures to prevent it worked out.
对承钢小方坯角裂产生的原因进行了剖析，并制订出相应的措施以减少裂纹。
Conversely tax rebates were cut down or removed on products featured with heavy energy consumption heavy pollution and resource-related such as billet rolled steel and aluminum not forged or rolled.
降低或取消了钢坯、钢材、未锻轧铝等高能耗、高污染和资源性产品的出口退税。
The high-efficiency reform of rectangular billet continuous caster of Xuanhua Iron and Steel Company is introduced, that can be used as reference for other continuous casters.
介绍了宣钢炼钢厂矩形坯连铸机的高效化改造，可供矩形坯、板坯连铸机高效化改造参考。
The paper introduces the billet production and existing problems of Q195 steel. Through practice, corresponding measures had been taken to gain good results.
介绍了Q 195钢小方坯生产的情况和存在问题，并提出了相应的解决办法，通过实践取得了较好的效果。
This paper introduces the application of dry magnesia-calcia coating and quick nozzle change technology in tundish of No. 1 billet caster at No. 2 Steel making Plant of Angang.
介绍安钢二炼钢厂在1号方坯连铸机中间罐上应用镁钙质干式涂料及快速更换水口技术的情况，快换水口系统原理及取得的效果。
Using flow field software PHOENICS and water model, this paper describes the flow field of molten steel in continuous casting billet mold.
应用流场计算软件PHOENICS及水力模型，模拟了方坯连铸结晶器内钢液的流场和流动分布。
There was no obvious oscillation mark on the billet surface. The average steel production of a copper tube was 3700 ton.
铸坯表面质量良好，单根铜管的平均过钢量为3700吨。
The new technologies of heating steel slab billet using natural gas as fuel and regenerative combustion way are mainly described, as well as obvious energy saving results are gained.
着重叙述了用天然气作燃料，采用蓄热式燃烧方式加热钢板坯的新技术，以及加热炉取得了显著节能效果。
In the end the relationship of steel grades, mould length, drawing speed and sectional dimensions of the billet with mould taper and solidification and contraction coefficient has been discussed.
最后分别讨论了钢种、结晶器长度、拉坯速度、铸坯断面尺寸与结晶器锥度、凝固收缩系数的关系。
The results showed that the major cause of reducing diameter was more non-metallic inclusion in the steel than standard value, billet segregation and shrinkage void.
用扫描电镜、大型金相显微镜观察分析高碳钢盘条的缩径，结果表明：造成缩径的主要原因是盘条中的非金属夹杂物超标、方坯偏析和缩孔。
The results showed that the major cause of reducing diameter was more non-metallic inclusion in the steel than standard value, billet segregation and shrinkage void.
用扫描电镜、大型金相显微镜观察分析高碳钢盘条的缩径，结果表明：造成缩径的主要原因是盘条中的非金属夹杂物超标、方坯偏析和缩孔。
应用推荐