The purpose of the research is to compare the effect of different alloying constituents on the stress corrosion sensitivity.
目的在于比较不同合金成分对应力腐蚀敏感性的影响。
The stress corrosion cracking sensitivity of the steel was low, and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.
研究表明该钢具有较好的抗应力腐蚀性能，其应力腐蚀断裂形貌为穿晶、解理断裂，并有二次裂纹。
The stress corrosion cracking sensitivity of the steel was low, and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.
研究表明该钢具有较好的抗应力腐蚀性能，其应力腐蚀断裂形貌为穿晶、解理断裂，并有二次裂纹。