By fracture analysis, this report presents the main causes for fracture failure of the crankshaft on overhauled Z12V190B diesel engines and puts forward some appropriate protective measures.
本文主要通过断口分析，找出了Z 12v190 B型柴油机大修后导致曲轴断裂失效的主要原因，并提出了相应的改进措施。
The failure analysis for universal shaft joint based on measuring results as well as fracture mechanic is carried out. And proposals of improving its endurance life are suggested.
以实测为根据，应用断裂理论对滑块式联接轴叉头进行了失效分析，并提出了提高疲劳寿命的措施。
The failure analysis for universal shaft joint based on measuring results as well as fracture mechanic is carried out.
以实测为根据，应用断裂理论对滑块式联接轴叉头进行了失效分析，并提出了提高疲劳寿命的措施。
Fracture failure analysis was made on resistance spot welding motor bracket test specimens which were destroyed by the high-frequency vibration.
分析了电阻点焊电动机支架高频振动破坏试样的失效原因。
The cracks on blades made of a directionally solidified superalloy were analyzed. The failure mode and cause were studied in virtue of fracture observation and metallographic analysis.
对定向凝固合金叶片的裂纹进行分析，在断口观察与金相组织分析的基础上，对叶片的失效模式与失效原因进行研究，并提出预防该类故障发生的措施。
Based on the failure analysis of reinforced concrete and the fracture behavior of concrete as a type of quasi-brittle materials, a model of matrix crack with bridging bar is proposed in this paper.
基于钢筋混凝土的破坏分析，结合混凝土类准脆性材料的断裂特性，本文提出了强化筋桥联基体裂纹力学分析模型，在该虚拟裂纹端部存在粘聚力分布，而强化筋在桥联裂纹处具有与基体脱离的部分段。
Based on the failure analysis of reinforced concrete and the fracture behavior of concrete as a type of quasi-brittle materials, a model of matrix crack with bridging bar is proposed in this paper.
基于钢筋混凝土的破坏分析，结合混凝土类准脆性材料的断裂特性，本文提出了强化筋桥联基体裂纹力学分析模型，在该虚拟裂纹端部存在粘聚力分布，而强化筋在桥联裂纹处具有与基体脱离的部分段。