The result showed that the direct reason of reboiler invalidation was the intercrystalline stress corrosion and crack caused by micro-chloride in the medium.
结果表明，介质中所含的微量氯离子引起的晶间型应力腐蚀开裂导致再沸器失效。
The result showed that the direct reason of reboiler invalidation was the intercrystalline stress corrosion and crack caused by micro-chloride in the medium.
结果表明，介质中所含的微量氯离子引起的晶间型应力腐蚀开裂导致再沸器失效。