Above this point the hardness can be increased only slightly, because steels above the eutectoid point are made up entirely of pearlite and cementite in the annealed state.
高于此点,由于超过共析点钢完全由珠光体和退火状态的渗碳体组成,硬度增加并不多。
It was found by experiments thatboron increased the growth rate of pearlite, both in hypoeutectoid and eutectoid steels.
硼有加速珠光体成长率的作用,无论在亚共析或共析钢中皆有同样的现象产生。
The resulting structure is a mixture of primary or pro-eutectoid ferrite (ferrite that formed above the eutectoid reaction) and regions of pearlite.
作为结果的组织结构是初步的共析铁素体(在共析反应前的铁素体)和部分珠光体的混合物。
By cr microalloying, the fore eutectoid ferrite eduction is restrained, the distance between rows of pearlite is decreased, then the tensile strength, section shrinkage and drawing property of high...
高碳钢中加入的铬元素抑制先共析铁素体析出,减小珠光体片层间距,可明显提高抗拉强度,提高断面收缩率,改善线材的拉拔性能。
Above this point the hardness can be increased only slightly, because steels above the eutectoid point are made up entirely of pearlite and cementite in the annealed state.
由于超过共析点钢完全由珠光体和退火状态的渗碳体组成,因此高于此点硬度增加并不多。
Above this point the hardness can be increased only slightly, because steels above the eutectoid point are made up entirely of pearlite and cementite in the annealed state.
由于超过共析点钢完全由珠光体和退火状态的渗碳体组成,因此高于此点硬度增加并不多。