The effects of five common set-retarders on setting time of cement paste and concrete and strength of concrete are studied.
论文分别研究了木钙、糖钙、酒石酸、焦磷酸钠和蔗糖共五种常用缓凝剂对水泥净浆凝结时间、混凝土凝结时间及强度的影响。
It is shown that the limestone powder with appropriate particle distribution can improve the fluidity of concrete, reduce bleeding rate and shorten the setting time.
试验结果表明：一定颗粒分布的石灰石粉能改善新拌混凝土的流动性能，减少泌水率及缩短凝结时间。
The setting time and soundness of samples accord with request.
凝结时间和安定性均符合要求。
Cement that has no additives to modify its setting time or rheological properties.
没有添加外加剂去改变其稠化时间或流变性能的水泥称之为净水泥。
The volume can be confirmed by curve of setting time and electrokinetic potential relation.
外加剂的掺量可由凝结时间一电动电位曲线确定。
The effect of bone glue protein retarder on setting time and strength of gypsum is studied.
研究了骨胶蛋白质石膏缓凝剂对石膏凝结时间和强度的影响。
The results showed that silicate can significantly speed up the setting time of cement grout.
试验结果表明，水玻璃能显著加快水泥浆的凝结时间。
Do not attempt to control setting time by increasing or decreasing the amount of catalyst dispensed.
不要试图通过增加或减少催化剂的用量来控制产品的凝固时间。
The effect of several fly ash with different amount and fineness on the setting time of cement is studied.
研究了不同掺量、不同细度的几种粉煤灰对水泥凝结时间的影响。
Quick: Don't need to weld and galvanize, the setting time is 3 times quicker than the flange connect fitting.
快速不需焊接和再镀锌，安装速度比法兰连接管件快3倍以上。
The effects of SAE on the density, absorbency, setting time and cement hydration of cement mortars were studied.
考察了SAE对水泥砂浆的密度、吸水性、凝结时间以及水泥水化速度的影响。
The maximum compression strength and setting time of the materials in experimental and control group were tested.
测定对照组和实验组的固化时间及最大抗压强度；
The effects of seeding on the setting time, the compressive strength and the microstructure of the CPC were studied.
研究两种晶种对骨水泥固化时间、抗压强度和产物微观结构的影响。
The effect of retarder on setting time, strength of hardened paste and crystallization habit of building gypsum was studied.
考察各种缓凝剂对建筑石膏凝结时间、硬化体强度以及结晶习性的影响。
The setting time of alkali-activated phosphor slag cement is short, but they all adjust to the standards of Portland cement.
碱磷渣胶凝材料的凝结时间较短，但都可以达到硅酸盐水泥标准。
The initial setting time of Portland cement shall not be earlier than 45 minutes, final set time not later than 390 minutes.
硅酸盐水泥的初凝时间不得早于45分钟，终凝时间不得迟于390分钟。
The results showed that the ultrafine slag did almost not influence the needed water of cement, but it postponed the setting time.
结果表明，矿渣细粉对水泥标准稠度需水量基本没有影响，但延长了水泥的凝结时间。
The effect of gypsum content on the hydration, compressive strength and setting time of Ba-bearing aluminoferriate cement was presented.
介绍了石膏含量对含钡铁铝酸盐水泥的水化、抗压强度和凝结时间等性能的影响。
Testing the setting time, flexural strength, compressive strength, water retention, adhesive strength of gypsum with the adhesive agents.
对掺加粘结剂的脱硫石膏的凝结时间、压折强度、保水性能、剪切粘结强度的测试。
When the s type retarder is added to the plaster, the setting time of plaster is delayed significantly and the strength is a little lower.
建筑石膏中掺入S型缓凝剂可使凝结时间显著延缓，但强度略有降低。
Finer grinding in a proper way will reduce the setting time of concrete made by shaft kiln cement containing F. However, it is impossible to...
适当细磨可以缩短含氟立窑水泥配制混凝土的凝结时间，但无法消除立窑水泥配制混凝土凝结时间偏长的缺点。
The results show that mobility of cement paste was improved after adding steel slag and setting time extends with the addition of steel slag increasing.
结果表明：钢渣的掺入可以改善水泥浆体的流动性，凝结时间随钢渣掺量增加而延长。
Prolonging the heat-setting time to provide enough relaxation time for high elastic strain, which can also reduce the inner stress and the dry heat-shrinkage.
延长定型时间有利于高弹形变的松弛，降低内应力，有利于降低干热收缩。
The results show that, with the in- crease in CA cement content, the fluidity of MgO-based investment materials decreases and so does the initial setting time.
结果表明，随着铝酸钙水泥含量的增加，氧化镁系包埋料的初凝时间缩短，流动性变差；
The results showed that the cement strength would be decreased and setting time increased drastically if the content of phosphor slag increased from 20% to 60%.
研究发现，磷渣掺量由20%增至60%时，水泥抗折和抗压强度均大幅下降，凝结时间随磷渣掺量增加而显著延长。
The cement setting time at different temperatures has been measured through choosing citric acid, sugar and sodium gluconate as the retarders of iron Portland cement.
通过选用柠檬酸、白糖、葡萄糖酸钠为矿渣硅酸盐水泥的缓凝剂，测定了不同温度下水泥的凝结时间，分析了温度对混凝土缓凝剂最优掺量的影响规律。
The results show that effect of gypsum on the setting time of different cements is similar and shaft kiln clinker is sensitive to gypsum larger than rotary kiln clinker.
研究结果表明，二水石膏对不同窑型水泥的凝结时间的影响类似，对立窑熟料的敏感性要大于回转窑熟料。
The results show that effect of gypsum on the setting time of different cements is similar and shaft kiln clinker is sensitive to gypsum larger than rotary kiln clinker.
研究结果表明，二水石膏对不同窑型水泥的凝结时间的影响类似，对立窑熟料的敏感性要大于回转窑熟料。