Manual molding had been used for the nodular iron front wheel boss and differential mechanism case, and chills were used to prevent shrinkage defects.

Results showed that ferrite net and lower hardness due to low cooling rate, coarser finish machining resulted in the fracture during earlier stage of rotary bending fatigue test.