The billet crack breakout would take place often in the process of continuous casting.
2
针对包钢连铸方坯的中心裂纹缺陷的形成原因进行分析,并提出减少中心裂纹的相应措施。
The article analyzes the causes of formation of central cracks of Bloom of Baogang and puts forward measures to decrease it.
3
从而验证了严重的结晶器磨损是连铸坯产生偏角区内裂纹乃至漏钢事故的重要原因之一。
These results verify that the severe mold wear is one of the most important reasons that induce the internal crack and even the breakout at the off-corner of billet.