魏氏组织

/ wèi shì zǔ zhī /

1
widmanstatten structure
魏氏组织 ( widmanstatten structure )：（共析钢没有），钢中相形态之一。凡是指亚共析钢中的先共析铁素体，或过共析钢中先渗碳体加珠光体的组织。
2
Widmannsttten structure
魏氏组织 widmannsttten structure; widmanstatenstructure 持组织镊 ti ue holding force; tissue grasping forceps; tissue holding forceps .

短语

1
有魏氏组织的试样较呈等轴铁素体的试样有更高的冲击韧性和更低的韧脆转变温度。
The specimens with Widmanstatten structure have higher impact strength and lower ductile-brittle transition temperature than those with equiaxial granular ferrite structure.
2
介绍了关魏氏组织形成的贝氏体型切变理论、类马氏体相变理论和扩散型台阶长大理论。
The theories about formation of Widmonstatten, Bainite shear and Martensite transformation are introduced, and the theory about growth of diffusion types of ledge is recommended as well.
3
结果表明，水龙头阀体开裂是由于存在过热造成的晶粒粗大、魏氏组织、铸造疏松等缺陷引起的脆性开裂。
The results show that the cracking of the tap valve is brittle crack, which is due to overheat to cause the formation of defects, such as coarse grains, Widmanstatten structure and porosity.

魏氏组织
魏氏组织是指在焊接的过热区内，由于奥氏体晶粒长得非常粗大，这种粗大的奥氏体在较快的冷却速度下会形成一种特殊的过热组织，其组织特征为在一个粗大的奥氏体晶粒内会形成许多平行的铁素体(渗碳体)针片，在铁素体针片之间的剩余奥氏体最后转变为珠光体，这种过热组织称为铁素体(渗碳体)魏氏组织。