With the increase temperature of the substrates, the added argon in the ambience of the reaction and the anneal after deposition, the crystal structure was better and the diffraction peak of the (002) surface was more strong.
随着衬底温度的升高、反应气氛中氩气含量的增加和退火处理,ZnO薄膜的结晶状况明显好转,(002)衍射峰的强度相对增强,且发光强度也得到一定的增强,光谱向紫外偏移。
参考来源 - 脉冲激光沉积制备ZnO薄膜及发光特性研究·2,447,543篇论文数据，部分数据来源于NoteExpress
Through theory analysis a mathmatical relation between martensitic {112} crystal plane diffraction peak is established.
通过讨论分析，建立了马氏体碳浓度与马氏体{112}晶面族衍射峰双线分离距离之间的关系式。
With the increasing of oxygen partial pressure, angle of (002) diffraction peak becomes larger and surface RMS of the films reduces.
随氧分压增加，（002）衍射峰的角度变大，表征薄膜表面粗糙程度的方均根粗糙度减小。
However, the diffraction peak of the original montmorillonite significantly shifts to small angle, the layer distance increases more than three times.
结果发现，经直接混炼之后，有机蒙脱土的衍射峰向小角度偏移很小，层间距没有明显变化；