Through-thickness cracking also can lead to fatigue or stress corrosion cracking of the base metal beneath the plating.
还会形成穿透型裂纹，造成镀层下本体金属的疲劳或应力腐蚀裂纹。
Stress concentrations can lead to initiation of cracking by fatigue, stress corrosion, or hydrogen-assisted stress corrosion.
应力集中可能会导致疲劳、应力腐蚀或氢基应力腐蚀而产生裂纹。
The fracture and the surface of a hip joint fractured invivo has been studied by SEM. It is concluded that the fracture was due to corrosion fatigue cracking by bending stress.
利用SEM对实际使用时断裂的髋关节的断口和表面进行了分析，认为此关节的断裂为以弯曲应力为主的腐蚀疲劳断裂。